mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE NANSHA/XP4034-BK1041
tensile strength	Yield	ASTM D638	62.0 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	88.0 Mpa
Bending modulus	50.0 mm Span	ASTM D790	2510 Mpa
elongation	Break	ASTM D638	25 %

injection	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE NANSHA/XP4034-BK1041
Suggested maximum moisture content			0.040 %
Mold temperature			55 to 70 °C
Processing (melt) temperature			260 to 275 °C
drying temperature			95 to 105 °C
Suggested injection volume			40 to 80 %
drying time			3.0 to 4.0 hr
Screw speed			30 to 80 rpm
Temperature in the middle of the barrel			245 to 260 °C
Temperature at the rear of the barrel			240 to 255 °C
Exhaust hole depth			0.038 to 0.076 mm
Temperature at the front of the material cylinder			250 to 265 °C
Back pressure			0.300 to 1.00 Mpa
Spray nozzle temperature			245 to 265 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE NANSHA/XP4034-BK1041
thermal conductivity		ASTM C177	0.25 W/m/K
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115 °C
Linear coefficient of thermal expansion	Across Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	104 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE NANSHA/XP4034-BK1041
Water absorption rate	24 hr	ASTM D570	0.25 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate		Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
melt mass-flow rate	280°C/3.8 kg	ASTM D1238	24 g/10 min

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	SABIC INNOVATIVE NANSHA/XP4034-BK1041
Rockwell hardness	R-Scale	ASTM D785	110