So sánh vật liệu

Thông tin sản phẩm
Tên sản phẩm
Tên thương hiệu
Lĩnh vực ứng dụng
Đặc tính
Giấy chứng nhận
Đơn giá
product

TPU-Ester Texin® 255 Covestro - Polycarbonates

--

--

--

- -
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Thông số kỹ thuật

impact performanceĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 255
Dart impact23°C,2.54mm,TotalEnergyASTM D376357.8 J
-30°C,2.54mm,TotalEnergyASTM D376350.0 J
flammabilityĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 255
UL flame retardant rating1.5mmUL 94HB
elastomerĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 255
Permanent compression deformation70°C,22hr3ISO 81535 %
Shore hardnessASTM D263240 %
Permanent compression deformation23°C,22hr3ASTM D395B15 %
elongationBreakASTM D412500 %
tensile strengthYieldISO 3763.4 MPa
Permanent compression deformation70°C,22hr3ASTM D395B35 %
100°C,22hr3ISO 81550 %
tensile strength300%StrainASTM D41232.4 MPa
Permanent compression deformation23°C,22hr3ISO 81515 %
100°C,22hrASTM D395B75 %
23°C,22hrISO 81520 %
tensile strength100%StrainISO 3715.9 MPa
elongationBreakISO 37500 %
Permanent compression deformation70°C,22hrISO 81565 %
70°C,22hrASTM D395B65 %
100°C,22hr3ASTM D395B50 %
tensile strength50%StrainASTM D41212.4 MPa
100%StrainASTM D41215.9 MPa
YieldASTM D41263.4 MPa
300%StrainISO 3732.4 MPa
50%StrainISO 3712.4 MPa
Permanent compression deformation23°C,22hrASTM D395B20 %
tear strengthISO 34-1160 kN/m
ASTM D624158 kN/m
Permanent compression deformation100°C,22hrISO 81575 %
mechanical propertiesĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 255
Bending modulus23°CISO 17868.9 MPa
shear strengthASTM D73238.5 MPa
Taber abraser1000Cycles,1000g,H-18WheelISO 464950.0 mg
1000Cycles,1000g,H-18WheelASTM D104450.0 mg
Bending modulus70°CISO 17851.7 MPa
23°CASTM D79068.9 MPa
-30°CASTM D7901210 MPa
-30°CISO 1781210 MPa
70°CASTM D79051.7 MPa
thermal performanceĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 255
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B59.0 °C
Vicat softening temperatureISO 306/50168 °C
Linear coefficient of thermal expansionMDASTM D6961.3E-04 cm/cm/°C
Hot deformation temperature0.45MPa,UnannealedASTM D64859.0 °C
Brittle temperatureISO 974<-68.0 °C
Glass transition temperatureDMA-26.0 °C
Brittle temperatureASTM D746<-68.0 °C
Vicat softening temperatureASTM D15255168 °C
Physical propertiesĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 255
Shrinkage rateMD：2.54mmASTM D9550.80 %
TD:2.54mmISO 25770.80 %
densityISO 11831.21 g/cm³
Shrinkage rateMD:2.54mmISO 25770.80 %
TD：2.54mmASTM D9550.80 %
densityASTM D7921.21 g/cm³
hardnessĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 255
Shore hardnessShoreDISO 86855
ShoreDASTM D224055
agingĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 255
Change rate of tensile strength in air100%Strain,23°C,504hr,inReferenceFuelA(Isooctane)ISO 1755.0 %
300%Strain,23°C,168hr,inReferenceFuelA(Isooctane)ASTM D471-11 %
Change rate of hardness (Shore) in the airShoreD,100°C,336hr,inASTM#1OilASTM D471-2.0
Change rate of tensile strength in air100%Strain,100°C,70hr,inASTM#1OilISO 17512 %
100°C,70hrASTM D5733.0 %
23°C,70hr,inReferenceFuelA(Isooctane)ASTM D4716.0 %
Volume change23°C,168hr,甲醇ASTM D47110 %
Shore hardnessShoreD,23°C,168hr,inReferenceFuelA(Isooctane)ISO 1751.0
Change rate of tensile strength in air300%Strain125°C,70hrISO 216-23 %
300%Strain,125°C,336hrASTM D573-27 %
Change rate of ultimate elongation in air100°C,336hr,inASTM#1OilASTM D47124 %
Change rate of tensile strength in air100%Strain,125°C,70hrASTM D5737.0 %
Tensile stress change rate23°C,168hr,inReferenceFuelA(Isooctane)，BreakISO 1759.0 %
100°C,504hr,inASTM#3Oil，BreakISO 17520 %
Change rate of tensile strength in air100%Strain100°C,504hrISO 21614 %
300%Strain,23°C,336hr,inReferenceFuelCASTM D471-35 %
100%Strain100°C,70hrISO 21611 %
100°C,336hrISO 21614 %
300%Strain,23°C,504hr,inReferenceFuelCASTM D471-28 %
Volume change23°C,70hr,inReferenceFuelAASTM D4710.0 %
Change rate of hardness (Shore) in the airShoreD,23°C,336hr,inReferenceFuelCASTM D471-6.0
Change rate of tensile strength in air100%Strain,100°C,70hr,inASTM#3OilASTM D47116 %
Change rate of hardness (Shore) in the airShoreD,23°C,504hr,inReferenceFuelCASTM D471-8.0
Change rate of ultimate elongation in air23°C,168hr,inReferenceFuelA(Isooctane)ASTM D4719.0 %
Change rate of tensile strength in air300%Strain,23°C,168hr,inReferenceFuelCASTM D471-34 %
300%Strain,23°C,70hr,inReferenceFuelA(Isooctane)ISO 1755.0 %
300%Strain,23°C,168hr,inReferenceFuelA(Isooctane)ISO 175-11 %
Volume change100°C,168hr,inASTM#1OilASTM D4710.0 %
Change rate of hardness (Shore) in the airShoreD,23°C,168hr,inReferenceFuelCASTM D471-4.0
Tensile stress change rate100°C,504hr,inASTM#1Oil，BreakISO 17516 %
Change rate of hardness (Shore) in the airShoreD,100°C,504hr,inASTM#3OilASTM D471-1.0
Change rate of tensile strength in air100°C,168hrASTM D5738.0 %
23°C,168hr,inReferenceFuelA(Isooctane)ISO 175-3.0 %
300%Strain100°C,504hrISO 2161.0 %
Volume change23°C,168hr,甲醇ISO 17510 %
Change rate of tensile strength in air300%Strain,125°C,504hrASTM D573-30 %
Volume change23°C,70hr,甲醇ASTM D4716.0 %
Change rate of hardness (Shore) in the airShoreD,100°C,70hr,inASTM#3OilASTM D4712.0
Volume change23°C,70hr,甲醇ISO 1756.0 %
Change rate of tensile strength in air300%Strain,100°C,168hr,inASTM#1OilISO 1752.0 %
300%Strain,125°C,168hrASTM D573-15 %
Shore hardnessShoreD,23°C,70hr,inReferenceFuelA(Isooctane)ISO 175-4.0
Change rate of tensile strength in air100%Strain,125°C,336hrASTM D5738.0 %
100%Strain,100°C,504hr,inASTM#3OilISO 1752.0 %
125°C,504hrASTM D573-27 %
100°C,168hr,inASTM#1OilASTM D471-4.0 %
Change rate of ultimate elongation in air125°C,168hrASTM D57324 %
Volume change100°C,70hr,在ASTM#3油中ASTM D4712.0 %
Tensile stress change rate100°C,504hr，BreakISO 21615 %
Volume change100°C,336hr,inASTM#1OilISO 175-1.0 %
Change rate of tensile strength in air300%Strain,100°C,70hr,inASTM#1OilISO 1757.0 %
Shore hardnessShoreD,100°C,504hr,inASTM#3OilISO 175-1.0
Change rate of tensile strength in air300%Strain,23°C,168hr,inReferenceFuelCISO 175-34 %
300%Strain,23°C,336hr,inReferenceFuelCISO 175-35 %
100%Strain,100°C,336hrASTM D57313 %
100%Strain,100°C,70hrASTM D57311 %
125°C,70hrISO 216-20 %
Shore hardnessShoreD,100°C,336hr,inASTM#1OilISO 175-2.0
Change rate of tensile strength in air100°C,336hrASTM D57314 %
300%Strain,100°C,336hr,inASTM#1OilASTM D471-9.0 %
100°C,336hr,inASTM#1OilISO 175-20 %
23°C,336hr,inReferenceFuelCASTM D471-10 %
Change rate of hardness (Shore) in the airShoreD,125°C,336hrASTM D573-5.0
Change rate of tensile strength in air125°C,70hrASTM D573-20 %
100°C,70hr,在ASTM#1油中ISO 17518 %
23°C,504hr,inReferenceFuelCASTM D471-11 %
300%Strain,23°C,504hr,inReferenceFuelCISO 175-28 %
100°C,504hr,inASTM#3OilASTM D471-18 %
100%Strain100°C,336hrISO 21613 %
100°C,336hr,inASTM#1OilASTM D471-20 %
100°C,504hrISO 21614 %
300%Strain100°C,70hrISO 2161.0 %
100%Strain,100°C,336hr,inASTM#1OilASTM D47114 %
Volume change100°C,70hr,在ASTM#1油中ISO 175-1.0 %
Change rate of tensile strength in air300%Strain,100°C,168hrASTM D573-5.0 %
Tensile stress change rate23°C,336hr,inReferenceFuelC，BreakISO 175-2.0 %
Change rate of ultimate elongation in air23°C,168hr,甲醇ASTM D4716.0 %
Change rate of tensile strength in air300%Strain,23°C,336hr,inReferenceFuelA(Isooctane)ASTM D471-1.0 %
Change rate of hardness (Shore) in the airShoreD,125°C,336hrISO 216-5.0
Change rate of tensile strength in air23°C,70hr,inReferenceFuelA(Isooctane)ISO 1756.0 %
100%Strain,23°C,504hr,inReferenceFuelA(Isooctane)ASTM D4715.0 %
300%Strain,100°C,70hr,inASTM#1OilASTM D4717.0 %
Change rate of ultimate elongation in air23°C,336hr,inReferenceFuelA(Isooctane)ASTM D471-4.0 %
Volume change100°C,504hr,inASTM#1OilASTM D471-1.0 %
Change rate of hardness (Shore) in the airShoreD,23°C,168hr,inReferenceFuelA(Isooctane)ASTM D4711.0
Change rate of tensile strength in air100%Strain,100°C,168hrASTM D5734.0 %
23°C,504hr,inReferenceFuelCISO 175-11 %
Shore hardnessShoreD,23°C,336hr,inReferenceFuelCISO 175-6.0
ShoreD,23°C,168hr,inReferenceFuelCISO 175-4.0
Tensile stress change rate100°C,336hr,inASTM#1Oil，BreakISO 17524 %
Change rate of ultimate elongation in air23°C,504hr,inReferenceFuelCASTM D471-8.0 %
100°C,504hr,inASTM#3OilASTM D47120 %
23°C,336hr,inReferenceFuelCASTM D471-2.0 %
Volume change23°C,336hr,inReferenceFuelCASTM D47114 %
23°C,504hr,inReferenceFuelCASTM D47114 %
23°C,168hr,inReferenceFuelAASTM D4710.0 %
23°C,336hr,inReferenceFuelAASTM D4710.0 %
Change rate of tensile strength in air100°C,70hrISO 2163.0 %
23°C,168hr,inReferenceFuelA(Isooctane)ASTM D471-3.0 %
Change rate of ultimate elongation in air23°C,70hr,inReferenceFuelA(Isooctane)ASTM D471-4.0 %
Change rate of tensile strength in air100%Strain,23°C,168hr,inReferenceFuelCISO 175-27 %
100%Strain,23°C,70hr,inReferenceFuelA(Isooctane)ISO 1752.0 %
300%Strain,23°C,336hr,inReferenceFuelA(Isooctane)ISO 175-1.0 %
100%Strain,100°C,336hr,inASTM#1OilISO 17514 %
300%Strain100°C,336hrISO 216-1.0 %
Tensile stress change rate125°C,168hr，BreakISO 21624 %
Shore hardnessShoreD,23°C,504hr,inReferenceFuelCISO 175-8.0
Change rate of tensile strength in air300%Strain,100°C,504hr,inASTM#3OilISO 175-12 %
100%Strain,125°C,504hrASTM D5734.0 %
Volume change23°C,504hr,inReferenceFuelAASTM D4710.0 %
Change rate of tensile strength in air23°C,168hr,甲醇ISO 175-4.0 %
Change rate of ultimate elongation in air125°C,336hrASTM D57335 %
Change rate of tensile strength in air100%Strain,23°C,70hr,inReferenceFuelA(Isooctane)ASTM D4712.0 %
Tensile stress change rate23°C,70hr,inReferenceFuelA(Isooctane)，BreakISO 175-4.0 %
Change rate of tensile strength in air100°C,70hr,在ASTM#3油中ASTM D47119 %
Volume change100°C,504hr,inASTM#3OilISO 1754.0 %
Change rate of tensile strength in air100%Strain,23°C,504hr,inReferenceFuelCISO 175-27 %
100%Strain,23°C,336hr,inReferenceFuelCISO 175-32 %
23°C,504hr,inReferenceFuelA(Isooctane)ISO 175-1.0 %
Tensile stress change rate23°C,504hr,inReferenceFuelC，BreakISO 175-8.0 %
Change rate of tensile strength in air125°C,168hrISO 216-11 %
23°C,336hr,inReferenceFuelCISO 175-10 %
Change rate of hardness (Shore) in the airShoreD,100°C,336hrISO 2160.0
Change rate of ultimate elongation in air100°C,70hr,在ASTM#3油中ASTM D4716.0 %
Tensile stress change rate23°C,70hr,甲醇，BreakISO 1755.0 %
Change rate of hardness (Shore) in the airShoreD,23°C,70hr,inReferenceFuelA(Isooctane)ASTM D471-4.0
Change rate of ultimate elongation in air125°C,504hrASTM D57330 %
Volume change100°C,504hr,inASTM#3OilASTM D4714.0 %
Change rate of hardness (Shore) in the airShoreD,100°C,70hrISO 216-2.0
Volume change100°C,168hr,inASTM#1OilISO 1750.0 %
100°C,70hr,在ASTM#3油中ISO 1752.0 %
Change rate of tensile strength in air300%Strain,100°C,504hrASTM D5731.0 %
Change rate of hardness (Shore) in the airShoreD,100°C,504hr,inASTM#1OilASTM D4710.0
Change rate of tensile strength in air300%Strain,23°C,504hr,inReferenceFuelA(Isooctane)ISO 1753.0 %
Change rate of hardness (Shore) in the airShoreD,100°C,168hrASTM D573-1.0
Tensile stress change rate100°C,70hr,在ASTM#3油中，BreakISO 1756.0 %
Change rate of tensile strength in air300%Strain125°C,504hrISO 216-30 %
300%Strain,23°C,70hr,inReferenceFuelCISO 175-22 %
Change rate of hardness (Shore) in the airShoreD,100°C,168hr,inASTM#1OilASTM D4711.0
Change rate of ultimate elongation in air100°C,504hr,inASTM#1OilASTM D47116 %
Change rate of tensile strength in air100%Strain125°C,336hrISO 2168.0 %
Shore hardnessShoreD,100°C,70hr,inASTM#3OilISO 1752.0
Change rate of hardness (Shore) in the airShoreD,100°C,70hr,inASTM#1OilASTM D4712.0
Change rate of tensile strength in air100°C,70hr,在ASTM#3油中ISO 17519 %
23°C,336hr,inReferenceFuelA(Isooctane)ISO 1756.0 %
23°C,504hr,inReferenceFuelA(Isooctane)ASTM D471-1.0 %
Change rate of hardness (Shore) in the airShoreD,23°C,504hr,inReferenceFuelA(Isooctane)ASTM D4716.0
Change rate of ultimate elongation in air100°C,168hr,inASTM#1OilASTM D47112 %
100°C,168hrASTM D5737.0 %
Change rate of tensile strength in air300%Strain,100°C,70hr,inASTM#3OilISO 17513 %
Volume change100°C,504hr,inASTM#1OilISO 175-1.0 %
Change rate of tensile strength in air23°C,70hr,甲醇ISO 1751.0 %
Change rate of hardness (Shore) in the air支撐D,125°C,168hrISO 2160.0
Volume change100°C,336hr,inASTM#1OilASTM D471-1.0 %
Tensile stress change rate23°C,168hr,甲醇，BreakISO 1756.0 %
Change rate of tensile strength in air100%Strain,23°C,336hr,inReferenceFuelCASTM D471-32 %
100%Strain,23°C,168hr,inReferenceFuelCASTM D471-27 %
100%Strain,23°C,70hr,inReferenceFuelCISO 175-19 %
300%Strain,100°C,504hr,inASTM#3OilASTM D471-12 %
100°C,504hrASTM D57314 %
Change rate of hardness (Shore) in the airShoreD,100°C,168hrISO 216-1.0
Change rate of tensile strength in air100%Strain,100°C,70hr,inASTM#3OilISO 17516 %
300%Strain,100°C,336hrASTM D573-1.0 %
100%Strain,23°C,504hr,inReferenceFuelCASTM D471-27 %
Change rate of hardness (Shore) in the airShoreD,100°C,504hrISO 2160.0
Change rate of tensile strength in air100%Strain125°C,168hrISO 216-2.0 %
300%Strain,100°C,336hr,inASTM#1OilISO 175-9.0 %
100%Strain,23°C,168hr,inReferenceFuelA(Isooctane)ISO 175-2.0 %
100%Strain125°C,504hrISO 2164.0 %
300%Strain,23°C,70hr,inReferenceFuelA(Isooctane)ASTM D4715.0 %
300%Strain,23°C,70hr,inReferenceFuelCASTM D471-22 %
Shore hardnessShoreD,23°C,504hr,inReferenceFuelA(Isooctane)ISO 1756.0
Change rate of hardness (Shore) in the air支撐D,125°C,168hrASTM D5730.0
Change rate of tensile strength in air300%Strain,100°C,70hrASTM D5731.0 %
Change rate of hardness (Shore) in the airShoreD,125°C,504hrASTM D573-4.0
Change rate of tensile strength in air300%Strain100°C,168hrISO 216-5.0 %
125°C,336hrISO 216-23 %
Tensile stress change rate23°C,336hr,inReferenceFuelA(Isooctane)，BreakISO 175-4.0 %
Change rate of tensile strength in air100°C,70hr,在ASTM#1油中ASTM D47118 %
100%Strain,100°C,70hr,inASTM#1OilASTM D47112 %
Tensile stress change rate125°C,336hr，BreakISO 21635 %
Change rate of tensile strength in air100°C,504hr,inASTM#3OilISO 175-18 %
100%Strain,100°C,504hr,inASTM#1OilASTM D47115 %
100%Strain,23°C,168hr,inReferenceFuelA(Isooctane)ASTM D471-2.0 %
Tensile stress change rate100°C,168hr，BreakISO 2167.0 %
Shore hardnessShoreD,100°C,168hr,inASTM#1OilISO 1751.0
Change rate of hardness (Shore) in the airShoreD,100°C,504hrASTM D5730.0
Change rate of ultimate elongation in air100°C,70hr,在ASTM#1油中ASTM D4718.0 %
Change rate of tensile strength in air300%Strain125°C,168hrISO 216-15 %
300%Strain,100°C,70hr,inASTM#3OilASTM D47113 %
Change rate of hardness (Shore) in the airShoreD,125°C,70hrISO 2161.0
Volume change23°C,70hr,inReferenceFuelAISO 1750.0 %
Change rate of tensile strength in air300%Strain,100°C,168hr,inASTM#1OilASTM D4712.0 %
100%Strain,23°C,336hr,inReferenceFuelA(Isooctane)ISO 1753.0 %
100%Strain,125°C,168hrASTM D573-2.0 %
100%Strain125°C,70hrISO 2167.0 %
100%Strain,100°C,168hr,inASTM#1OilASTM D47114 %
100°C,168hr,inASTM#1OilISO 175-4.0 %
Volume change23°C,336hr,inReferenceFuelCISO 17514 %
Change rate of tensile strength in air125°C,168hrASTM D573-11 %
Shore hardnessShoreD,23°C,336hr,inReferenceFuelA(Isooctane)ISO 175-1.0
Tensile stress change rate100°C,70hr,在ASTM#1油中，BreakISO 1758.0 %
Volume change23°C,168hr,inReferenceFuelAISO 1750.0 %
Tensile stress change rate100°C,70hr，BreakISO 216-3.0 %
Volume change23°C,504hr,inReferenceFuelAISO 1750.0 %
Change rate of hardness (Shore) in the airShoreD,125°C,504hrISO 216-4.0
Volume change23°C,336hr,inReferenceFuelAISO 1750.0 %
23°C,504hr,inReferenceFuelCISO 17514 %
Change rate of ultimate elongation in air125°C,70hrASTM D57328 %
Change rate of hardness (Shore) in the airShoreD,23°C,70hr,inReferenceFuelCASTM D471-7.0
Change rate of tensile strength in air100%Strain,100°C,504hr,inASTM#1OilISO 17515 %
100%Strain,23°C,336hr,inReferenceFuelA(Isooctane)ASTM D4713.0 %
300%Strain,100°C,504hr,inASTM#1OilISO 175-14 %
100%Strain,23°C,70hr,inReferenceFuelCASTM D471-19 %
Change rate of hardness (Shore) in the airShoreD,125°C,70hrASTM D5731.0
Change rate of tensile strength in air100%Strain100°C,168hrISO 2164.0 %
100°C,504hr,inASTM#1OilISO 175-29 %
100%Strain,100°C,504hr,inASTM#3OilASTM D4712.0 %
Shore hardnessShoreD,100°C,504hr,inASTM#1OilISO 1750.0
Change rate of tensile strength in air23°C,168hr,甲醇ASTM D471-4.0 %
Change rate of ultimate elongation in air100°C,336hrASTM D57314 %
100°C,504hrASTM D57315 %
Change rate of hardness (Shore) in the airShoreD,100°C,70hrASTM D573-2.0
Change rate of tensile strength in air300%Strain125°C,336hrISO 216-27 %
300%Strain,125°C,70hrASTM D573-23 %
100°C,168hrISO 2168.0 %
Tensile stress change rate100°C,168hr,inASTM#1Oil，BreakISO 17512 %
Change rate of tensile strength in air100%Strain,100°C,168hr,inASTM#1OilISO 17514 %
100%Strain,100°C,504hrASTM D57314 %
Shore hardnessShoreD,23°C,70hr,inReferenceFuelCISO 175-7.0
Tensile stress change rate23°C,504hr,inReferenceFuelA(Isooctane)，BreakISO 175-2.0 %
Change rate of hardness (Shore) in the airShoreD,100°C,336hrASTM D5730.0
Change rate of ultimate elongation in air23°C,504hr,inReferenceFuelA(Isooctane)ASTM D471-2.0 %
Change rate of tensile strength in air100°C,504hr,inASTM#1OilASTM D471-29 %
23°C,336hr,inReferenceFuelA(Isooctane)ASTM D4716.0 %
Shore hardnessShoreD,100°C,70hr,inASTM#1OilISO 1752.0
Change rate of tensile strength in air125°C,336hrASTM D573-23 %
Change rate of hardness (Shore) in the airShoreD,23°C,336hr,inReferenceFuelA(Isooctane)ASTM D471-1.0
Volume change100°C,70hr,在ASTM#1油中ASTM D471-1.0 %
Change rate of tensile strength in air300%Strain,23°C,504hr,inReferenceFuelA(Isooctane)ASTM D4713.0 %
Tensile stress change rate100°C,336hr，BreakISO 21614 %
Change rate of ultimate elongation in air100°C,70hrASTM D573-3.0 %
Change rate of tensile strength in air23°C,70hr,甲醇ASTM D4711.0 %
300%Strain,100°C,504hr,inASTM#1OilASTM D471-14 %
125°C,504hrISO 216-27 %
Change rate of ultimate elongation in air23°C,70hr,甲醇ASTM D4715.0 %
Tensile stress change rate125°C,70hr，BreakISO 21628 %
125°C,504hr，BreakISO 21630 %
Supplementary InformationĐiều kiện kiểm traPhương pháp kiểm traCovestro - Polycarbonates/Texin® 255
CompressiveLoad15%DeflectionASTM D57510.1 MPa
25%DeflectionASTM D57515.5 MPa
10%DeflectionASTM D5757.41 MPa
5%DeflectionASTM D5753.90 MPa
50%DeflectionASTM D57540.6 MPa
20%DeflectionASTM D57512.7 MPa
2%DeflectionASTM D5750.965 MPa