PP Starpylen MX05039 EUROSTAR FRANCE

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	50 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	5.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	5.0 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	50 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	36.0 MPa
Bending modulus	Bending modulus	ISO 178	1900 MPa
elongation	elongation Yield	ASTM D638	3.9 %
tensile strength	tensile strength Break	ISO 527-2/50	18.0 MPa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	22.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	1900 MPa
elongation	elongation Yield	ASTM D638	3.9 %
tensile strength	tensile strength Break	ISO 527-2/50	18.0 MPa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	22.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	1900 MPa
bending strength	bending strength	ISO 178	36.0 MPa
Bending modulus	Bending modulus	ISO 178	1900 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	63.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	99.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to60°C	ISO 11359-2	1.4E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to60°C	ISO 11359-2	1.1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to60°C	ISO 11359-2	1.1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to60°C	ISO 11359-2	1.4E-04 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	99.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	63.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.030 %
Shrinkage rate	Shrinkage rate MD：4.00mm	Internal Method	1.1 %
density	density	ISO 1183	1.05 g/cm³
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.030 %
Shrinkage rate	Shrinkage rate MD：4.00mm	Internal Method	1.1 %
density	density	ISO 1183	1.05 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.