PC LEXAN™ 1414T NA8A005T SABIC INNOVATIVE NANSHA

Đặc tính:
Chịu nhiệt độ thấp
Trong suốt
Dễ dàng xử lý
Dòng chảy trung bình
Lĩnh vực ứng dụng:
Thiết bị gia dụng
Nắp chai
Lĩnh vực điện tử
Lĩnh vực điện
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	60 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	无断裂
Dart impact	Dart impact 23°C, Total Energy	ASTM D3763	76.0 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --3	ASTM D638	2240 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	2300 Mpa
tensile strength	tensile strength Yield4	ASTM D638	59.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	57.0 Mpa
		tensile strength	tensile strength Break4	ASTM D638	51.0 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	54.0 Mpa
elongation	elongation Yield4	ASTM D638	5.8 %
	elongation	elongation Yield	ISO 527-2/50	5.4 %
		elongation	elongation Break4	ASTM D638	84 %
		elongation	elongation	elongation Break	ISO 527-2/50	110 %
Bending modulus	Bending modulus 50.0 mm Span5	ASTM D790	2220 Mpa
Bending modulus	Bending modulus	Bending modulus --6	ISO 178	2150 Mpa
bending strength	bending strength --6,7	ISO 178	89.0 Mpa
bending strength	bending strength	bending strength Yield, 50.0 mm Span5	ASTM D790	85.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	120 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	40 to 60 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	215 to 295 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	280 to 305 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	295 to 315 °C
Spray nozzle temperature	Spray nozzle temperature	290 to 310 °C
Processing (melt) temperature	Processing (melt) temperature	295 to 315 °C
Mold temperature	Mold temperature	70 to 95 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	40 to 70 rpm
Exhaust hole depth	Exhaust hole depth	0.025 to 0.076 mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	122 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10	ISO 75-2/Af	116 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D152511	138 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	142 °C
Ball Pressure Test	Ball Pressure Test 123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 95°C	ASTM E831	6.7E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : 23 to 80°C	ISO 11359-2	6.7E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 95°C	ASTM E831	8.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : 23 to 80°C	ISO 11359-2	8.0E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 300°C/1.2 kg	ASTM D1238	10 g/10 min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2 kg	ISO 1133	9.00 cm3/10min
Shrinkage rate	Shrinkage rate Flow 2	Internal Method	0.40 - 0.80 %
	Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.40 - 0.80 %
	Shrinkage rate	Shrinkage rate	Shrinkage rate Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80 %
Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.12 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.090 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.