PBT Romiloy® 5250 GF 20 ROMIRA GERMANY

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	42 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	7.0 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	6.0 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	7.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	42 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	50 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	6.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	50 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.6mm

UL 94

UL flame retardant rating

1.6mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength 23°C	ISO 178	150 MPa
Bending modulus	Bending modulus 23°C	ISO 178	5360 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	6.5 %
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	6500 MPa
Bending modulus	Bending modulus 23°C	ISO 178	5360 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	6.5 %
tensile strength	tensile strength Yield,23°C	ISO 527-2/5	96.0 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	6500 MPa
tensile strength	tensile strength Yield,23°C	ISO 527-2/5	96.0 MPa
bending strength	bending strength 23°C	ISO 178	150 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	145 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	145 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Vicat softening temperature

ISO 306/B50

145 °C

Vicat softening temperature

ISO 306/B50

145 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.36 g/cm³
Shrinkage rate	Shrinkage rate 23°C	ISO 294-4	0.40to0.60 %
melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ISO 1133	30 g/10min
density	density	ISO 1183	1.36 g/cm³
Shrinkage rate	Shrinkage rate 23°C	ISO 294-4	0.40to0.60 %
melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ISO 1133	30 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.