PC/PBT XENOY™ 1760-7100 SABIC INNOVATIVE JAPAN

102

Đặc tính:
Kháng hóa chất
Dòng chảy cao
Gia cố sợi thủy tinh
Chống va đập cao
Lĩnh vực ứng dụng:
Phụ tùng ô tô bên ngoài
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dart impact	Dart impact 23°C, Total Energy	ASTM D3763	8.00 J
	Dart impact	Dart impact -20°C, Energy at Peak	ASTM D3763	4.00 J
		Dart impact	Dart impact -30°C, Total Energy	ASTM D3763	3.00 J
		Dart impact	Dart impact	Dart impact -30°C, Energy at Peak	ASTM D3763	3.00 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield, 50.0 mm Span3	ASTM D790	131 Mpa
bending strength	bending strength	bending strength --4,5	ISO 178	133 Mpa
Bending modulus	Bending modulus --4	ISO 178	4010 Mpa
Bending modulus	Bending modulus	Bending modulus 50.0 mm Span3	ASTM D790	3910 Mpa
elongation	elongation Break	ISO 527-2/5	3.0 %
	elongation	elongation Break2	ASTM D638	3.0 %
		elongation	elongation Yield	ISO 527-2/5	3.0 %
		elongation	elongation	elongation Yield2	ASTM D638	3.0 %
tensile strength	tensile strength Break	ISO 527-2/5	84.0 Mpa
	tensile strength	tensile strength Break2	ASTM D638	84.0 Mpa
		tensile strength	tensile strength Yield	ISO 527-2/5	84.0 Mpa
		tensile strength	tensile strength	tensile strength Yield2	ASTM D638	84.0 Mpa
Tensile modulus	Tensile modulus --	ISO 527-2/1	4800 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --1	ASTM D638	5310 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	50 to 80 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	250 to 270 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	255 to 275 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	260 to 280 °C
Spray nozzle temperature	Spray nozzle temperature	255 to 275 °C
Processing (melt) temperature	Processing (melt) temperature	260 to 280 °C
Mold temperature	Mold temperature	65 to 95 °C
Back pressure	Back pressure	0.300 to 0.600 Mpa
Screw speed	Screw speed	50 to 80 rpm
Exhaust hole depth	Exhaust hole depth	0.013 to 0.020 mm
drying temperature	drying temperature	110 °C
drying time	drying time	4.0 to 6.0 hr

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	125 °C
	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	116 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	101 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D15258	121 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	135 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	130 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	3.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	7.6E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40°C	ISO 11359-2	7.6E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.50 %
Shrinkage rate	Shrinkage rate Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.60 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.40 - 0.60 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 265°C/5.0 kg	ISO 1133	27.0 cm3/10min
melt mass-flow rate	melt mass-flow rate 250°C/5.0 kg	ASTM D1238	15 g/10 min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.