mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break3	ASTM D638	6.1 %
elongation	elongation	elongation Break	ISO 527-2/50	7.1 %
Bending modulus	Bending modulus 50.0mmSpan4	ASTM D790	2520 Mpa
Bending modulus	Bending modulus	Bending modulus --5	ISO 178	2470 Mpa
bending strength	bending strength --5,6	ISO 178	103 Mpa
bending strength	bending strength	bending strength Yield,50.0mmSpan4	ASTM D790	100 Mpa
Tensile modulus	Tensile modulus --2	ASTM D638	2420 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	2670 Mpa
tensile strength	tensile strength Yield3	ASTM D638	65.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	66.0 Mpa
		tensile strength	tensile strength Break3	ASTM D638	63.0 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	64.0 Mpa
elongation	elongation Yield3	ASTM D638	3.8 %
elongation	elongation	elongation Yield	ISO 527-2/50	4.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to60°C	ISO 11359-2	8.6E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	187 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan9	ISO 75-2/Bf	184 °C
Vicat softening temperature	Vicat softening temperature --	ASTMD152510	197 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	198 °C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to40°C	ASTME831	7.6E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to60°C	ISO 11359-2	8.1E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to40°C	ASTME831	7.8E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 300°C/5.0kg	ASTM D1238	7.8 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/5.0kg	ISO 1133	7.00 cm3/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	1.3-1.5 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	4.0 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.40 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	Internal Method	1.0E+3-1.0E+4 ohms·cm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

Internal Method

1.0E+3-1.0E+4 ohms·cm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.