mechanical properties	Test Condition	Test Method	Test Result
tensile strength	tensile strength Yield	ASTM D638	54.0 Mpa
elongation	elongation Break	ASTM D638	75 %
Bending modulus	Bending modulus 50.0 mm Span	ASTM D790	2300 Mpa
bending strength	bending strength Yield, 50.0 mm Span	ASTM D790	84.0 Mpa

injection	Test Condition	Test Result
drying temperature	drying temperature	105 to 110 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.040 %
Suggested injection volume	Suggested injection volume	30 to 80 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	250 to 290 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	255 to 295 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	260 to 300 °C
Spray nozzle temperature	Spray nozzle temperature	275 to 300 °C
Processing (melt) temperature	Processing (melt) temperature	275 to 300 °C
Mold temperature	Mold temperature	60 to 90 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	40 to 70 rpm
Exhaust hole depth	Exhaust hole depth	0.038 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 3.20 mm	ASTM D648	123 °C
	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm	ASTM D648	129 °C
		Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	107 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	110 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15254	129 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
thermal conductivity	thermal conductivity	ASTM C177	0.20 W/m/K
RTI Elec	RTI Elec	UL 746	60.0 °C
RTI Imp	RTI Imp	UL 746	60.0 °C
RTI	RTI	UL 746	60.0 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	melt mass-flow rate 260°C/5.0 kg	ASTM D1238	17 g/10 min
Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Water absorption rate	Water absorption rate 24 hr	ASTM D570	0.10 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 23°C	ASTM D570	0.40 %

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance	Arc resistance	ASTM D495	PLC 6
Compared to the anti leakage trace index	Compared to the anti leakage trace index	UL 746	PLC 2
High arc combustion index	High arc combustion index	UL 746	PLC 0
Hot wire ignition	Hot wire ignition	UL 746	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	118

hardness

Test Condition

Test Method

Test Result

Rockwell hardness

R-Scale

ASTM D785

118

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.