impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	17 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	59 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	320 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	4.5 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	19 kJ/m²
Dart impact	Dart impact -30°C,TotalEnergy	ASTM D3763	20.0 J
Dart impact	Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	35.0 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	1790 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	2000 Mpa
tensile strength	tensile strength Yield	ASTM D638	41.4 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	39.0 Mpa
		tensile strength	tensile strength Break	ASTM D638	34.5 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	29.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2/50	3.1 %
elongation	elongation Break	ASTM D638	40 %
Tensile strain	Tensile strain Break	ISO 527-2/50	44 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	1790 Mpa
Bending modulus	Bending modulus	Bending modulus	ISO 178	2000 Mpa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	58.6 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	87.8 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	90.6 °C
		Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	91.0 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	76.7 °C
RTI Imp	RTI Imp	UL 746	50.0 °C
RTI Str	RTI Str	UL 746	50.0 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	79.4 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	80.0 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ASTM D648	95.6 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15259	99.4 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ISO 306/B50	90.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to0°C	ASTME831	8.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	8.6E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：0to100°C	ASTME831	9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	9.2E-05 cm/cm/°C
RTI Elec	RTI Elec	UL 746	50.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ASTM D1238	7.0 g/10min
	melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ASTM D1238	13 g/10min
	melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 280°C/3.8kg	ASTM D1238	20 g/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Water absorption rate Equilibrium,23°C	ASTM D570	0.55 %
Outdoor applicability	Outdoor applicability	UL 746C	f2
density	density	ASTM D792	1.06 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 0
High arc combustion index	High arc combustion index HAI	UL 746	PLC 0
Hot wire ignition	Hot wire ignition HWI	UL 746	PLC 3
Surface resistivity	Surface resistivity	ASTM D257	>1.0E+15 ohms
Dielectric strength	Dielectric strength 3.20mm,inOil	ASTM D149	16 KV/mm
Dielectric constant	Dielectric constant 50Hz	ASTM D150	5.20
	Dielectric constant	Dielectric constant 60Hz	ASTM D150	5.20
	Dielectric constant	Dielectric constant	Dielectric constant 1MHz	ASTM D150	3.21
Dissipation factor	Dissipation factor 50Hz	ASTM D150	0.15
	Dissipation factor	Dissipation factor 60Hz	ASTM D150	0.15
	Dissipation factor	Dissipation factor	Dissipation factor 1MHz	ASTM D150	0.026

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	86

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.