impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	56 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	30 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	65 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/1A	21 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	2330 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	2350 Mpa
tensile strength	tensile strength Yield	ASTM D638	47.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	49.0 Mpa
	tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	40.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2/50	3.9 %
elongation	elongation Break	ASTM D638	70 %
Tensile strain	Tensile strain Break	ISO 527-2/50	75 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2200 Mpa
Bending modulus	Bending modulus	Bending modulus	ISO 178	2100 Mpa
bending strength	bending strength	ISO 178	75.0 Mpa
bending strength	bending strength	bending strength Yield,50.0mmSpan	ASTM D790	77.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	118 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	120 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	96.0 °C
			Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	101 °C
			Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	96.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	112 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	114 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ASTM D1238	25 g/10min
melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ISO 1133	9.0 g/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

melt mass-flow rate

260°C/5.0kg

ASTM D1238

25 g/10min

melt mass-flow rate

220°C/10.0kg

ISO 1133

9.0 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.