flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	UL flame retardant rating 1.5 mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating 6.0 mm	UL 94	V-0
Radiation board grade	Radiation board grade		RP100

flammability

Test Condition

Test Method

Test Result

UL flame retardant rating

1.5 mm

UL 94

V-1

UL flame retardant rating

6.0 mm

UL 94

V-0

Radiation board grade

RP100

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	tensile strength Yield	ASTM D638	67.0 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	53.0 Mpa
elongation	elongation Yield	ASTM D638	8.1 %
elongation	elongation	elongation Break	ASTM D638	20 %
Bending modulus	Bending modulus 100 mm Span	ASTM D790	2500 Mpa
bending strength	bending strength Yield, 100 mm Span	ASTM D790	102 Mpa

injection	Test Condition	Test Result
drying temperature	drying temperature	105 to 110 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	30 to 70 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	250 to 300 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	260 to 305 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	270 to 310 °C
Spray nozzle temperature	Spray nozzle temperature	280 to 310 °C
Processing (melt) temperature	Processing (melt) temperature	280 to 310 °C
Mold temperature	Mold temperature	75 to 105 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	20 to 100 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm	ASTM D648	126 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	117 °C
RTI Elec	RTI Elec	UL 746	110 °C
RTI Imp	RTI Imp	UL 746	105 °C
RTI	RTI	UL 746	110 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Across FlowFlow 2	Internal Method	0.50 - 0.70 %
Water absorption rate	Water absorption rate 24 hr	ASTM D570	0.060 %
Outdoor applicability	Outdoor applicability	UL 746C	f1

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity	Surface resistivity	ASTM D257	> 1.0E+15 ohms
Volume resistivity	Volume resistivity	ASTM D257	2.3E+16 ohms·cm
Dielectric strength	Dielectric strength 3.20 mm, in Oil	ASTM D149	18 KV/mm
Dielectric constant	Dielectric constant 60 Hz	ASTM D150	2.52
	Dielectric constant	Dielectric constant 50 kHz	ASTM D150	2.52
	Dielectric constant	Dielectric constant	Dielectric constant 1 MHz	ASTM D150	2.46
Dissipation factor	Dissipation factor 50 Hz	ASTM D150	3.4E-3
	Dissipation factor	Dissipation factor 60 Hz	ASTM D150	3.4E-3
	Dissipation factor	Dissipation factor	Dissipation factor 1 MHz	ASTM D150	2.1E-3
Arc resistance	Arc resistance	ASTM D495	PLC 6
Compared to the anti leakage trace index	Compared to the anti leakage trace index	UL 746	PLC 1
High voltage arc tracing rate	High voltage arc tracing rate	UL 746	PLC 4

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PPO NORYL™ SE1X-701 SABIC INNOVATIVE US