impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	16 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	14 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of cantilever beam gap

23°C

ISO 180/1A

16 kJ/m²

Charpy Notched Impact Strength

23°C

ISO 179/1eA

14 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break	ASTM D638	12 %
Tensile strain	Tensile strain Break	ISO 527-2/50	12 %
Bending modulus	Bending modulus	ASTM D790	2200 Mpa
tensile strength	tensile strength Break	ISO 527-2/50	37.0 Mpa
	tensile strength	tensile strength Break	ASTM D638	36.0 Mpa
		tensile strength	tensile strength Yield	ISO 527-2/50	49.0 Mpa
		tensile strength	tensile strength	tensile strength Yield	ASTM D638	43.0 Mpa
Tensile modulus	Tensile modulus	ISO 527-2/50	2200 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	1900 Mpa
Bending modulus	Bending modulus	ISO 178	2400 Mpa
bending strength	bending strength	ASTM D790	67.0 Mpa
bending strength	bending strength	bending strength	ISO 178	70.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	103 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	101 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed,4.00mm	ISO 75-2/A	102 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,4.00mm	ISO 75-2/A	80.0 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	90.0 °C
			Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed,4.00mm	ISO 75-2/B	106 °C
				Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,4.00mm	ISO 75-2/B	96.0 °C
				Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	97.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD:3.20mm	ISO 2577	0.40-0.70 %
	Shrinkage rate	Shrinkage rate TD:3.20mm	ISO 2577	0.40-0.70 %
		Shrinkage rate	Shrinkage rate TD：3.20mm	ASTM D955	0.40-0.70 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD：3.20mm	ASTM D955	0.40-0.70 %
melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ISO 1133	6.0 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ASTM D1238	6.0 g/10min

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ISO 2039-2	106
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	105

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ISO 2039-2

106

Rockwell hardness

R-Scale

ASTM D785

105

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.