Material Description

Material Properties:Chống cháy｜Gia cố sợi thủy tinh｜Ổn định nhiệt｜Chịu nhiệt độ cao
Typical Applications:Hộp đựng thực phẩm
Color:--
Grade:Lớp ép phun

Technical Data Sheet Compare

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap Dry，-40℃	ISO 180/1A	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength Dry，23℃	ISO 179/1eA	95 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength Dry	ISO 179/1eA	15 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap Dry，23℃	ISO 180/1A	236 °C

mechanical properties	Test Condition	Test Method	Test Result
Poisson's ratio	Poisson's ratio Dry	ISO 527-1/-2	14
Tensile modulus	Tensile modulus Dry	ISO 527-1/-2	16500 Mpa
Tensile modulus	Tensile modulus	Tensile modulus Conditio	ISO 527-1/-2	16300 Mpa
Bending modulus	Bending modulus Dry	ISO 178	15000 Mpa
Elongation at Break	Elongation at Break Dry	ISO 527-1/-2	2.8 %
Elongation at Break	Elongation at Break	Elongation at Break Conditio	ISO 527-1/-2	3.2 %
tensile strength	tensile strength Dry，Break	ISO 527-1/-2	250 Mpa
tensile strength	tensile strength	tensile strength Conditione，Break	ISO 527-1/-2	215 Mpa

thermal properties	Test Condition	Test Method	Test Result
Melting temperature	Melting temperature	ISO 11357-1/-3	260 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -40-23°C，Across Flow	ISO 11359-1/-2	55 E-6/K
RTI Elec	RTI Elec	UL 746B	65 °C
	RTI Elec	RTI Elec	UL 746B	65 °C
	RTI Elec	RTI Elec	RTI Elec	UL 746B	65 °C
RTI Imp	RTI Imp	UL 746B	65 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow	ISO 11359-1/-2	55 E-6/K
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -40-23°C，Flow	ISO 11359-1/-2	17 E-6/K
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-1/-2	14 E-6/K
RTI Imp	RTI Imp	UL 746B	65 °C
RTI Imp	RTI Imp	RTI Imp	UL 746B	65 °C

combustion performance	Test Condition	Test Method	Test Result
UL flame retardant rating	UL flame retardant rating HB	UL 94	0.75 mm
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating HB	UL 94	1.5 mm
Limiting Oxygen Index (LOI)	Limiting Oxygen Index (LOI)	ISO 4589-1/-2	27 %
FMVSS combustion rate	FMVSS combustion rate	FMVSS 302	B -
Burning rate	Burning rate 1mm	ISO 3795	25 mm/min

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Shrinkage rate Dry，Flow	ISO 294-4	0.2 %
Shrinkage rate	Shrinkage rate Dry	ISO 294-4	0.4 %

Physical properties

Test Condition

Test Method

Test Result

Shrinkage rate

Dry，Flow

ISO 294-4

0.2 %

Shrinkage rate

Dry

ISO 294-4

0.4 %

Electrical Property	Test Condition	Test Method	Test Result
Volume resistivity	Volume resistivity	IEC 60093	10000000000000 Ohm-m
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI)	IEC 60112	600 -

Electrical Property

Test Condition

Test Method

Test Result

Volume resistivity

IEC 60093

10000000000000 Ohm-m

Compared to the Leakage Traceability Index (CTI)

IEC 60112

600 -

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.