mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 1/4〃 Notched	ASTM D-256	1.5 kg.cm/cm
Bending modulus	Bending modulus	ASTM D-790	40000 kg/cm
elongation	elongation	ASTM D-638	8 %
bending strength	bending strength	ASTM D-790	1350 kg/cm
tensile strength	tensile strength	ASTM D-638	720 kg/cm
Rockwell hardness	Rockwell hardness	ASTM D-785	122 R
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 1/8" Notched	ASTM D-256	2.0 kg.cm/cm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Combustibility	Combustibility 1/16〃	UL -94	HB
Combustibility	Combustibility	Combustibility 1/8"	UL -94	HB
Hot deformation temperature	Hot deformation temperature Unannealed 18.5kg/cm	ASTM D-648	98 °C
Vicat softening temperature	Vicat softening temperature 1000g	ASTM D-1525	107 °C
Combustibility	Combustibility 1/8	IEC 707	FH3-25 mm/min

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 220℃ 5kg	ASTM D-1238	2.5 g/10min
melt mass-flow rate	melt mass-flow rate 220℃ 10kg	ASTM D-1238	25 g/10min
Shrinkage rate	Shrinkage rate	ASTM D-955	0.2-0.6

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

melt mass-flow rate

220℃ 5kg

ASTM D-1238

2.5 g/10min

melt mass-flow rate

220℃ 10kg

ASTM D-1238

25 g/10min

Shrinkage rate

ASTM D-955

0.2-0.6

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.