flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	UL flame retardant rating 0.75mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating 2.0mm	UL 94	5VB

flammability

Test Condition

Test Method

Test Result

UL flame retardant rating

0.75mm

UL 94

V-2

UL flame retardant rating

1.5mm

UL 94

V-0

UL flame retardant rating

2.0mm

UL 94

5VB

mechanical properties	Test Condition	Test Method	Test Result
elongation	elongation Break	ASTM D638	80 %
elongation	elongation	elongation Yield	ASTM D638	4.0 %
tensile strength	tensile strength Break	ASTM D638	49.0 Mpa
tensile strength	tensile strength	tensile strength Yield	ASTM D638	63.0 Mpa
Tensile modulus	Tensile modulus	ASTM D638	3000 Mpa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	94.0 Mpa
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2620 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Str	RTI Str	UL 746	80.0 °C
RTI Imp	RTI Imp	UL 746	70.0 °C
RTI Elec	RTI Elec	UL 746	80.0 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15255	99.0 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	90.0 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	83.0 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	98.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Water absorption rate 24hr	ASTM D570	0.11 %
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.40-0.60 %
melt mass-flow rate	melt mass-flow rate 260°C/2.16kg	ASTM D1238	22 g/10min

Physical properties

Test Condition

Test Method

Test Result

Water absorption rate

24hr

ASTM D570

0.11 %

Shrinkage rate

MD：3.20mm

Internal Method

0.40-0.60 %

melt mass-flow rate

260°C/2.16kg

ASTM D1238

22 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	Relative permittivity 1MHz	IEC 60250	2.70
	Relative permittivity	Relative permittivity 60Hz	IEC 60250	2.70
	Relative permittivity	Relative permittivity	Relative permittivity 50Hz	IEC 60250	2.70
Dielectric strength	Dielectric strength 3.20mm,in Oil	IEC 60243-1	17 KV/mm
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	>1.0E+15 ohms
Dissipation factor	Dissipation factor 50Hz	IEC 60250	4E-03
	Dissipation factor	Dissipation factor 60Hz	IEC 60250	4E-03
	Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	6E-03

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.