optical performance	Test Condition	Test Method	Test Result
gloss	gloss 45°，20.3um	ASTM D-2457	70
gloss	gloss	gloss 45°，50.8um	ASTM D-2457	67
turbidity	turbidity 20.3um	ASTM D-1003	7 %
turbidity	turbidity	turbidity 50.8um	ASTM D-1003	10 %
gloss	gloss 45°	ASTM D2457	34
turbidity	turbidity	ASTM D1003	20 %

Other performance	Test Condition	Test Method	Test Result
Film toughness	Film toughness 20.3um，TD	ASTM D-882	304 J/cm³
	Film toughness	Film toughness 20.3um，MD	ASTM D-882	240 J/cm4
		Film toughness	Film toughness 50.8um，MD	ASTM D-882	273 J/cm5
		Film toughness	Film toughness	Film toughness 50.8um，TD	ASTM D-882	292 J/cm6
Thin film puncture strength	Thin film puncture strength 20.3um	Internal Method	11.4 J/cm³
Thin film puncture strength	Thin film puncture strength	Thin film puncture strength 50.8um	Internal Method	9.76 J/cm³

machinability	Test Condition	Test Method	Test Result
Melt Temperature	Melt Temperature		221-232 °C

machinability

Test Condition

Test Method

Test Result

Melt Temperature

221-232 °C

Basic Performance	Test Condition	Test Method	Test Result
density	density	ASTM D-792	0.922 g/m3
melt mass-flow rate	melt mass-flow rate 190℃/2.16kg	ASTM D-1238	1 g/10min

Basic Performance

Test Condition

Test Method

Test Result

density

ASTM D-792

0.922 g/m3

melt mass-flow rate

190℃/2.16kg

ASTM D-1238

1 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Elmendorf tear strength	Elmendorf tear strength 50.8um，MD	ASTM D-1922	740 g
	Elmendorf tear strength	Elmendorf tear strength 50.8um，TD	ASTM D-1922	1200 g
		Elmendorf tear strength	Elmendorf tear strength 20.3um，MD	ASTM D-1922	440 g
		Elmendorf tear strength	Elmendorf tear strength	Elmendorf tear strength 20.3um，TD	ASTM D-1922	580 g
Dart impact	Dart impact 50.8um	ASTM D-1709A	280 g
Dart impact	Dart impact	Dart impact 20.3um	ASTM D-1709A	130 g
Elongation at Break	Elongation at Break 50.8um，MD	ASTM D-882	670 %
	Elongation at Break	Elongation at Break 50.8um，TD	ASTM D-882	770 %
		Elongation at Break	Elongation at Break 20.3um，TD	ASTM D-882	750 %
		Elongation at Break	Elongation at Break	Elongation at Break 20.3um，MD	ASTM D-882	480 %
tensile strength	tensile strength 50.8um，TD,Break	ASTM D-882	44.3 Mpa
	tensile strength	tensile strength 50.8um，MD,Break	ASTM D-882	51.9 Mpa
		tensile strength	tensile strength 20.3um，TD,Break	ASTM D-882	49.2 Mpa
			tensile strength	tensile strength 20.3um，MD,Break	ASTM D-882	60.4 Mpa
				tensile strength	tensile strength 50.8um，Yield,TD	ASTM D-882	12.6 Mpa
					tensile strength	tensile strength 50.8um，Yield,MD	ASTM D-882	11.8 Mpa
						tensile strength	tensile strength 20.3um，Yield,MD	ASTM D-882	12.7 Mpa
						tensile strength	tensile strength	tensile strength 20.3um，Yield,TD	ASTM D-882	13.1 Mpa
Secant modulus	Secant modulus 2% Secant，50.8um，TD	ASTM D-882	234 Mpa
	Secant modulus	Secant modulus 2% Secant，50.8um，MD	ASTM D-882	196 Mpa
		Secant modulus	Secant modulus 20.3um，TD	ASTM D-882	247 Mpa
		Secant modulus	Secant modulus	Secant modulus 20.3um，MD	ASTM D-882	227 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	Vicat softening temperature	ASTM D-1525	104 °C
Melting temperature	Melting temperature	Internal Method	122 °C
Vicat softening temperature	Vicat softening temperature	ASTM D1525	104 °C
Melting temperature	Melting temperature	Internal Method	122 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	melt mass-flow rate 190°C/2.16kg	ASTM D1238	1.0 g/10min

Physical properties

Test Condition

Test Method

Test Result

melt mass-flow rate

190°C/2.16kg

ASTM D1238

1.0 g/10min

film	Test Condition	Test Method	Test Result
film thickness	film thickness	Internal Method	25 µm
Thin film puncture strength	Thin film puncture strength	Internal Method	1.24 J
	Thin film puncture strength	Thin film puncture strength	Internal Method	31.1 N
	Thin film puncture strength	Thin film puncture strength	Thin film puncture strength	Internal Method	6.21 J/cm³
Membrane strength	Membrane strength MD	ASTM D882	110 J/cm³
Membrane strength	Membrane strength	Membrane strength TD	ASTM D882	114 J/cm³
Secant modulus	Secant modulus 1%Secant,MD	ASTM D882	211 Mpa
	Secant modulus	Secant modulus 2%Secant,MD	ASTM D882	172 Mpa
		Secant modulus	Secant modulus 1%Secant,TD	ASTM D882	234 Mpa
		Secant modulus	Secant modulus	Secant modulus 2%Secant,TD	ASTM D882	189 Mpa
Dart impact	Dart impact	ASTM D1709A	180 g
Elmendorf tear strength	Elmendorf tear strength MD	ASTM D1922	440 g
Elmendorf tear strength	Elmendorf tear strength	Elmendorf tear strength TD	ASTM D1922	630 g
tensile strength	tensile strength MD:Yield	ASTM D882	13.4 Mpa
	tensile strength	tensile strength TD:Yield	ASTM D882	14.1 Mpa
		tensile strength	tensile strength MD:Break	ASTM D882	46.1 Mpa
		tensile strength	tensile strength	tensile strength TD:Break	ASTM D882	35.3 Mpa
elongation	elongation MD:Break	ASTM D882	540 %
elongation	elongation	elongation TD:Break	ASTM D882	660 %

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.