impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	34.2 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	16 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	7.8 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	16 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Break	ISO 527-2/50	53.3 Mpa
	tensile strength	tensile strength Break	ASTM D638	51.3 Mpa
		tensile strength	tensile strength Yield	ISO 527-2/50	64.9 Mpa
		tensile strength	tensile strength	tensile strength Yield	ASTM D638	63.3 Mpa
Tensile modulus	Tensile modulus	ISO 527-2/1	2910 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	2170 Mpa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	104 Mpa
elongation	elongation Yield	ASTM D638	5.2 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	4.9 %
elongation	elongation Break	ASTM D638	29 %
Tensile strain	Tensile strain Break	ISO 527-2/50	21 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2630 Mpa
Bending modulus	Bending modulus	Bending modulus	ISO 178	2630 Mpa
bending strength	bending strength	ISO 178	107 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	7.4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	7.1E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	7.1E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	7.4E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	138 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	136 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ASTM D152510	136 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	116 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	115 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.050 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.25 %
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.50-0.80 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/5.0kg	ISO 1133	9.85 cm3/10min
melt mass-flow rate	melt mass-flow rate 280°C/5.0kg	ASTM D1238	9.6 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.