mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Elongation at Break	Elongation at Break 23℃	ASTM D-638	3.0 %
tensile strength	tensile strength Yield,23℃	ASTM D-638	127 Mpa
Rockwell hardness	Rockwell hardness	ASTM D-785	116 R scale
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃,6.40mm	ASTM D-256	69.0 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30℃,6.40mm	ASTM D-256	39.0 J/m
bending strength	bending strength 23℃	ASTM D-790	142 Mpa
Bending modulus	Bending modulus 23℃	ASTM D-790	7350 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating	UL 94	HB
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ASTM D-696	0.000041 cm/cm/℃
Vicat softening temperature	Vicat softening temperature	ASTM D-1525	120 °C
Hot deformation temperature	Hot deformation temperature 1.80MPa，Unannealed，6.40mm	ASTM D-648	100 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate Flow	ASTM D-955	0.20-0.30 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

Flow

ASTM D-955

0.20-0.30 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.