PPO NORYL GTX™  GTX979 BK SABIC INNOVATIVE US

82
  • Unit Price:
    US $ 5,656 /MT
  • Packaging Specification:
    25KG/túi
  • Packaging Material:
    Keo dán túi
  • Supply Quantity:
    5MT (1 Container | Container MT / 20Feet)
  • COA Certificate:
    Provide
  • Delivery Terms:
    CIF
  • Port Of Destination:
    Saigon Port
Material Description
Technical Data Sheet

Material Description

  • Material Properties:Dòng chảy caoKích thước ổn địnhChịu nhiệt độ caoChống thủy phân
  • Typical Applications:Ứng dụng điệnMáy móc công nghiệpỨng dụng trong lĩnh vực ô
  • Color:--
  • Grade:Lớp ép phun

Technical Data Sheet Compare

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength

Charpy Notched Impact Strength

-30°C

ISO 179/1eA12 kJ/m²
Charpy Notched Impact Strength

Charpy Notched Impact Strength

23°C

ISO 179/1eA20 kJ/m²
Suspended wall beam without notch impact strength

Suspended wall beam without notch impact strength

-30°C

ISO 180/1U无断裂
Suspended wall beam without notch impact strength

Suspended wall beam without notch impact strength

23°C

ISO 180/1U无断裂
Dart impact

Dart impact

23°C,TotalEnergy

ASTM D376350.0 J
flammabilityTest ConditionTest MethodTest Result
Burning wire flammability index

Burning wire flammability index

3.2mm

IEC 60695-2-12650 °C
mechanical propertiesTest ConditionTest MethodTest Result
tensile strength

tensile strength

Break4

ASTM D63850.0 Mpa
tensile strength

tensile strength

Break

ISO 527-2/5050.0 Mpa
elongation

elongation

Yield4

ASTM D6385.0 %
elongation

elongation

Yield

ISO 527-2/504.0 %
elongation

elongation

Break4

ASTM D63860 %
elongation

elongation

Break

ISO 527-2/5030 %
Bending modulus

Bending modulus

50.0mmSpan5

ASTM D7902050 Mpa
Bending modulus

Bending modulus

--6

ISO 1782150 Mpa
bending strength

bending strength

--6,7

ISO 17880.0 Mpa
bending strength

bending strength

Yield,50.0mmSpan5

ASTM D79080.0 Mpa
Tensile modulus

Tensile modulus

--3

ASTM D6382000 Mpa
Tensile modulus

Tensile modulus

--

ISO 527-2/12100 Mpa
tensile strength

tensile strength

Yield4

ASTM D63855.0 Mpa
tensile strength

tensile strength

Yield

ISO 527-2/5055.0 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature

Hot deformation temperature

0.45MPa,Unannealed,100mmSpan10

ISO 75-2/Be178 °C
Vicat softening temperature

Vicat softening temperature

--

ASTMD152511180 °C
Vicat softening temperature

Vicat softening temperature

--

ISO 306/B120182 °C
Linear coefficient of thermal expansion

Linear coefficient of thermal expansion

MD:-40to40°C

ASTME8319.5E-05 cm/cm/°C
Linear coefficient of thermal expansion

Linear coefficient of thermal expansion

MD:23to80°C

ISO 11359-29.6E-05 cm/cm/°C
Linear coefficient of thermal expansion

Linear coefficient of thermal expansion

TD:-40to40°C

ASTME8311E-04 cm/cm/°C
Linear coefficient of thermal expansion

Linear coefficient of thermal expansion

TD:23to80°C

ISO 11359-29.6E-05 cm/cm/°C
Hot deformation temperature

Hot deformation temperature

0.45MPa,Unannealed,3.20mm

ASTM D648185 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate

melt mass-flow rate

280°C/5.0kg

ASTM D123815 g/10min
Melt Volume Flow Rate (MVR)

Melt Volume Flow Rate (MVR)

280°C/5.0kg

ISO 113311.0 cm3/10min
Shrinkage rate

Shrinkage rate

MD:3.20mm

Internal Method1.2-1.6 %
Shrinkage rate

Shrinkage rate

TD:3.20mm

Internal Method1.2-1.6 %
Water absorption rate

Water absorption rate

Saturation,23°C

ISO 624.2 %
Water absorption rate

Water absorption rate

Equilibrium,23°C,50%RH

ISO 621.2 %
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivity

Volume resistivity

Internal Method1.0E+3-1.0E+4 ohms·cm
IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.