PA11 Rilsan® BESVO A FDA ARKEMA FRANCE

Unit Price:
₫ 293.900 /KG
Packaging Specification:
25KG/túi
Packaging Material:
Túi giấy
Supply Quantity:
27.8MT
COA Certificate:
Provide
Place of Delivery:
Miền Nam Việt Nam (xung quanh Hồ Chí Minh)

Material Description

Material Properties:Chống tia cực tím｜Ổn định nhiệt
Typical Applications:Dây điện｜Hồ sơ
Color:--
Grade:Lớp ép phun

Technical Data Sheet Compare

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	--
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	--

impact performance

Test Condition

Test Method

Test Result

Impact strength of simply supported beam without notch

-30°C

ISO 179/1eU

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

flammability	Test Condition	Test Method	Test Result
Flammability level	Flammability level	UL 94	V-2
Flammability level	Flammability level	UL 94	V-2
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	25 %

flammability

Test Condition

Test Method

Test Result

Flammability level

UL 94

V-2

Flammability level

UL 94

V-2

Extreme Oxygen Index

ISO 4589-2

25 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	Tensile modulus	ISO 527-2	1420 Mpa
Tensile stress	Tensile stress Yield	ISO 527-2	41 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2	5.0 %
elongation	elongation Break	ISO 527-2	＞50 %
tensile strength	tensile strength Yield	ISO 527-2	41.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2	5.0 %
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	> 50 %

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Hot deformation temperature 0.45MPa	ISO 75-2	145 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa	ISO 75-2	50 °C
Vicat softening temperature	Vicat softening temperature	ISO 306	160 °C
Melting temperature	Melting temperature	ISO 11357-3	189 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	ISO 11359-2	0.000085 cm/cm/℃
UL flame retardant rating	UL flame retardant rating	ISO 1210	V-2
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	25 %
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed	ISO 75-2/B	145 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ISO 75-2/A	50.0 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	160 °C
Melting temperature	Melting temperature	ISO 11357-3	189 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	8.5E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	melt mass-flow rate	ISO 1133	6.0 cm3/10min
Water absorption rate	Water absorption rate Saturation	ISO 62	1.9 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 235°C/10.0 kg	ISO 1133	6.00 cm3/10min
Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	1.9 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	Dielectric strength	IEC 60243-1	-- KV/mm

Electrical performance

Test Condition

Test Method

Test Result

Dielectric strength

IEC 60243-1

-- KV/mm

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.