PA46 Stanyl® TW371 DSM HOLAND

Unit Price:
₫ 390.590 /KG
Packaging Specification:
25KG/túi
Packaging Material:
Túi giấy
Supply Quantity:
10MT
COA Certificate:
Provide
Place of Delivery:
Miền Nam Việt Nam (xung quanh Hồ Chí Minh)

Material Description

Material Properties:Bôi trơn｜Ổn định nhiệt
Typical Applications:Bộ phận gia dụng｜Linh kiện điện tử
Color:--
Grade:Lớp ép phun

Technical Data Sheet Compare

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	7.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/1A	5.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	150 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	7.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	5.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
Flammability level	Flammability level	UL 94	HB
Flammability level	Flammability level	UL 94	HB

flammability

Test Condition

Test Method

Test Result

Flammability level

UL 94

Flammability level

UL 94

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	Bending modulus	ISO 178	2600 Mpa
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	30 %
tensile strength	tensile strength Yield	ISO 527-2	90.0 Mpa
Tensile modulus	Tensile modulus	ISO 527-2	2900 Mpa

thermal performance	Test Condition	Test Method	Test Result
Thermal Index - 5000 hr	Thermal Index - 5000 hr	IEC 60216	152 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow	ISO 11359-2	1.1E-4 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	8.5E-5 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	295 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ISO 75-2/A	190 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed	ISO 75-2/B	290 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	3.2 %
Shrinkage rate	Shrinkage rate Flow	ISO 294-4	2.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate 横向Flow	ISO 294-4	2.0 %
density	density	ISO 1183	1.25 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 1
Volume resistivity	Volume resistivity	IEC 60093	1.0E+14 ohms·cm

Electrical performance

Test Condition

Test Method

Test Result

Compared to the anti leakage trace index

IEC 60112

PLC 1

Volume resistivity

IEC 60093

1.0E+14 ohms·cm

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.