ABS

ABS POLYLAC® PA-758 TAIWAN CHIMEI

299

Unit Price:
US $ 2,521 /MT
Packaging Specification:
25KG/túi
Packaging Material:
Keo dán túi
Supply Quantity:
20MT (1 Container | Container 20MT / 20Feet)
COA Certificate:
Provide
Delivery Terms:
CIF
Port Of Destination:
Saigon Port
Material Comparison:
ABS TR557 LG CHEM KOREA

Recent Transactions:

November 18, 2025 , 63.720 VND/KG(25 KG)

Material Description

Material Properties:Trong suốt
Typical Applications:Hàng gia dụng｜Bộ phận gia dụng｜Lĩnh vực ô tô
Color:--
Grade:Lớp trong suốt

Material Certification

SGS

RoHS

MSDS

SGS

TDS

MSDS

RoHS

SVHC

Processing

Statement

Technical Data Sheet Compare

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	14 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	7.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.40mm	ASTM D256	160 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.20mm	ASTM D256	150 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	14 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179	7.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

flammability

Test Condition

Test Method

Test Result

UL flame retardant rating

1.5mm

UL 94

mechanical properties	Test Condition	Test Method	Test Result
bending strength	bending strength --4	ASTM D790	53.9 Mpa
Bending modulus	Bending modulus --5	ISO 178	1900 Mpa
Bending modulus	Bending modulus	Bending modulus --4	ASTM D790	1900 Mpa
elongation	elongation Break	ISO 527-2/50	40 %
elongation	elongation	elongation Break3	ASTM D638	40 %
tensile strength	tensile strength --3	ASTM D638	39.7 Mpa
	tensile strength	tensile strength Break	ISO 527-2/50	33.0 Mpa
	tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	42.0 Mpa
bending strength	bending strength --5	ISO 178	57.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	97.0 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D15256	105 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	104 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	96.0 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ASTM D648	99.0 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	77.0 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	88.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	9E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Shrinkage rate	ISO 294-4	0.30-0.70 %
melt mass-flow rate	melt mass-flow rate 200°C/5.0kg	ASTMD1238	3.0 g/10min
density	density 23°C	ISO 1183	1.08 g/cm³
density	density	density --	ASTM D792	1.08 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	107

hardness

Test Condition

Test Method

Test Result

Rockwell hardness

R-Scale

ASTM D785

107

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.