mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D-638	2070 Mpa
tensile strength	tensile strength Yield	ASTM D-638	40.7 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D-638	31.7 Mpa
elongation at yield	elongation at yield	ASTM D-638	3.0 %
Elongation at Break	Elongation at Break	ASTM D-638	24 %
Bending modulus	Bending modulus 50.0mm Span	ASTM D-790	2140 Mpa
bending strength	bending strength 50.0mm Span，Yield	ASTM D-790	62.1 Mpa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	ASTM D-256	160 J/m

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa，Unannealed，3.20mm	ASTM D-648	87.8 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.80MPa，Unannealed，3.20mm	ASTM D-648	77.8 °C
Vicat softening temperature	Vicat softening temperature	ASTM D-1525	99.4 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow,-40TO40℃	ASTM E-831	0.000086 cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Transverse,-40TO40℃	ASTM E-831	0.000092 cm/cm/℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate Flow,3.20mm	ASTM D-955	0.50-0.70 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

Flow,3.20mm

ASTM D-955

0.50-0.70 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.