mechanical properties	Test Condition	Test Method	Test Result
Rockwell hardness	Rockwell hardness	ASTM D-785	110 M Scale
bending strength	bending strength dry(moist)	ASTM D-790	260(220) Mpa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap dry(moist)	ASTM D-256	80(90) J/m
elongation	elongation dry(moist)	ASTM D-638	3(3) %
tensile strength	tensile strength dry(moist)	ASTM D-638	170(140) Mpa
Bending modulus	Bending modulus dry(moist)	ASTM D-790	10000(7000) Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Hot deformation temperature HDT	ASTM D-648	300 °C
Melting temperature	Melting temperature		310 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	ASTM D-696	2.4(5.0)
UL flame retardant rating	UL flame retardant rating	UL 94	HB
Glass transition temperature (Tg)	Glass transition temperature (Tg)		85 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Shrinkage rate 2mmt	ASTM D-955	0.5(0.8) %

Physical properties

Test Condition

Test Method

Test Result

Shrinkage rate

2mmt

ASTM D-955

0.5(0.8) %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	Dielectric strength dry	ASTM D-149	28 KV/mm
Dissipation factor	Dissipation factor 10	ASTM D-150	0.018
Dielectric constant	Dielectric constant 10	ASTM D-150	4.5
Volume resistivity	Volume resistivity dry	ASTM D-257	10 Ω.cm

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.