POM DURACON®  M90-44 TAIWAN POLYPLASTICS

34
  • Unit Price:
    US $ 1,740 /MT
  • Packaging Specification:
    25KG/túi
  • Packaging Material:
    Túi giấy
  • Supply Quantity:
    16MT (1 Container | Container 16MT / 20Feet)
  • COA Certificate:
    Provide
  • Delivery Terms:
    CIF
  • Port Of Destination:
    Saigon Port
  • Material Comparison:
    POM FORMOCON®  FM090 FPC TAIWAN
Material Description
Material Certification
Technical Data Sheet

Material Description

  • Material Properties:Độ nhớt cao｜Chống mài mòn｜Trong suốt｜Dòng chảy cao｜Thời tiết kháng｜phổ quát
  • Typical Applications:Lĩnh vực điện｜Lĩnh vực điện tử｜Thiết bị gia dụng｜Thiết bị gia dụng
  • Color:--
  • Grade:Lớp ép phun

Material Certification

UL
SGS

Technical Data Sheet Compare

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength

Charpy Notched Impact Strength

23°C

ISO 179/1eA6.0 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating

UL flame retardant rating

UL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus

Tensile modulus

ISO 527-22700 Mpa
tensile strength

tensile strength

ISO 527-262.0 Mpa
Nominal tensile fracture strain

Nominal tensile fracture strain

ISO 527-235 %
Bending modulus

Bending modulus

ISO 1782500 Mpa
bending strength

bending strength

ISO 17887.0 Mpa
Friction coefficient

Friction coefficient

Dynamic2

JISK72180.37
Friction coefficient

Friction coefficient

Steel - Dynamic3

JISK72180.46
Friction coefficient

Friction coefficient

Steel - Dynamic4

JISK72180.40
Wear factor

Wear factor

0.98MPa,0.30m/sec5

JISK7218<1.0 10^-8mm³/N·m
Wear factor

Wear factor

0.49MPa,0.30m/sec5

JISK7218<1.0 10^-8mm³/N·m
Wear factor

Wear factor

0.98MPa,0.30m/sec6

JISK721830 10^-8mm³/N·m
Wear factor

Wear factor

0.49MPa,0.30m/sec6

JISK721865 10^-8mm³/N·m
Wear factor

Wear factor

0.060MPa,0.15m/sec7

JISK72183500 10^-8mm³/N·m
Wear factor

Wear factor

0.060MPa,0.15m/sec8

JISK72186500 10^-8mm³/N·m
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature

Hot deformation temperature

1.8MPa,Unannealed

ISO 75-2/A95.0 °C
Linear coefficient of thermal expansion

Linear coefficient of thermal expansion

MD：23to55°C

Internal Method1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion

Linear coefficient of thermal expansion

TD：23to55°C

Internal Method1.2E-04 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
density

density

ISO 11831.41 g/cm³
melt mass-flow rate

melt mass-flow rate

ASTM D12389.0 g/10min
melt mass-flow rate

melt mass-flow rate

ISO 11339.0 g/10min
Melt Volume Flow Rate (MVR)

Melt Volume Flow Rate (MVR)

190°C/2.16kg

ISO 11338.00 cm3/10min
Shrinkage rate

Shrinkage rate

TD:2.00mm

ISO 294-42.0 %
Shrinkage rate

Shrinkage rate

MD:2.00mm

ISO 294-42.0 %
Water absorption rate

Water absorption rate

23°C,24hr

ISO 620.50 %
Electrical performanceTest ConditionTest MethodTest Result
Surface resistivity

Surface resistivity

IEC 600931E+16 ohms
Volume resistivity

Volume resistivity

IEC 600931E+14 ohms·cm
Dielectric strength

Dielectric strength

3.00mm

IEC 60243-119 KV/mm
hardnessTest ConditionTest MethodTest Result
Rockwell hardness

Rockwell hardness

M-Scale

ISO 2039-280
Supplementary InformationTest ConditionTest MethodTest Result
ColourNumber

ColourNumber

CF2001/CD3068
IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.