mechanical properties	Test Condition	Test Method	Test Result
Elongation at Break	Elongation at Break	ASTM D638/ISO 527	》200 %
tensile strength	tensile strength	ASTM D638/ISO 527	23 kg/cm²(MPa)[Lb/in²]
Rockwell hardness	Rockwell hardness	ASTM D785	86
Bending modulus	Bending modulus	ASTM D790/ISO 178	970 kg/cm²(MPa)[Lb/in²]
Rockwell hardness	Rockwell hardness	ASTM D-785	75 R-Scale
Bending modulus	Bending modulus	ASTM D-790A	1300 Mpa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20℃	ASTM D-256	70 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	ASTM D-256	NB J/m
elongation	elongation Break	ASTM D-638	>200 %
tensile strength	tensile strength Yield	ASTM D-638	26.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	Vicat softening temperature	ASTM D1525/ISO R306	65 ℃（℉）
Hot deformation temperature	Hot deformation temperature 0.46MPa	ASTM D-648	93 °C

thermal performance

Test Condition

Test Method

Test Result

Vicat softening temperature

ASTM D1525/ISO R306

65 ℃（℉）

Hot deformation temperature

0.46MPa

ASTM D-648

93 °C

Physical properties	Test Condition	Test Method	Test Result
density	density	ASTM D792/ISO 1183	0.093
melt mass-flow rate	melt mass-flow rate	ASTM D1238/ISO 1133	2.5 g/10min

Physical properties

Test Condition

Test Method

Test Result

density

ASTM D792/ISO 1183

0.093

melt mass-flow rate

ASTM D1238/ISO 1133

2.5 g/10min

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.