Material Description

Material Properties:Chịu nhiệt độ cao｜Gia cố sợi thủy tinh
Typical Applications:Thiết bị tập thể dục｜Thiết bị điện｜Trang trí ngoại thất ô tô
Color:--
Grade:Lớp ép phun

Technical Data Sheet Compare

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	45 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	7 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	8 kJ/m²
Bending modulus	Bending modulus 23°C	ISO 178	10300 Mpa
Tensile modulus	Tensile modulus 23°C	ISO 527-2	11600 Mpa
Elongation at Break	Elongation at Break 23°C	ISO 527-2	2.10 %
tensile strength	tensile strength 23°C	ISO 527-2	187 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	6.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	2.1E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature Melting Temperature	ISO 11357-3	310 °C
Hot deformation temperature	Hot deformation temperature 1.80MPaAnnealed	ISO 75-2/Af	285 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.90 %
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.30 %

Physical properties

Test Condition

Test Method

Test Result

Shrinkage rate

ISO 294-4

0.90 %

Shrinkage rate

ISO 294-4

0.30 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	Dielectric strength 0.250mm	IEC 60243-1	28 KV/mm
Volume resistivity	Volume resistivity	IEC 60093	1E+14 Ω.cm

Electrical performance

Test Condition

Test Method

Test Result

Dielectric strength

0.250mm

IEC 60243-1

28 KV/mm

Volume resistivity

IEC 60093

1E+14 Ω.cm

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating	UL flame retardant rating	UL -94	HB 0.75mm
	UL flame retardant rating	UL flame retardant rating	UL -94	HB 1.50mm
	UL flame retardant rating	UL flame retardant rating	UL flame retardant rating	UL -94	HB 3.00mm
Relative temperature of heating wire	Relative temperature of heating wire 3.00mm	IEC 60695-2-13	850 °C
	Relative temperature of heating wire	Relative temperature of heating wire 1.50mm	IEC 60695-2-13	700 °C
	Relative temperature of heating wire	Relative temperature of heating wire	Relative temperature of heating wire 0.75mm	IEC 60695-2-13	750 °C
Ignition temperature of heating wire	Ignition temperature of heating wire 3.00mm	IEC 60695-2-12	775 °C
	Ignition temperature of heating wire	Ignition temperature of heating wire 1.50mm	IEC 60695-2-12	725 °C
	Ignition temperature of heating wire	Ignition temperature of heating wire	Ignition temperature of heating wire 0.75mm	IEC 60695-2-12	775 °C

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.