flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 6.0 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating 2.5 mm	UL 94	5VA
	UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.5 mm	UL 94	V-1
Extreme Oxygen Index	Extreme Oxygen Index	ASTM D2863	31 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield, 100 mm Span	ASTM D790	151 Mpa
Bending modulus	Bending modulus 100 mm Span	ASTM D790	5720 Mpa
elongation	elongation Break	ASTM D638	5.0 %
tensile strength	tensile strength Break	ASTM D638	106 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	110 to 120 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	30 to 70 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	265 to 315 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	275 to 320 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	290 to 325 °C
Spray nozzle temperature	Spray nozzle temperature	300 to 325 °C
Processing (melt) temperature	Processing (melt) temperature	300 to 325 °C
Mold temperature	Mold temperature	80 to 110 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	20 to 100 rpm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI	RTI	UL 746	110 °C
RTI Imp	RTI Imp	UL 746	105 °C
RTI Elec	RTI Elec	UL 746	110 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -40 to 95°C，Flow	ASTM E831	3.6E-5 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 24 hr	ASTM D570	0.060 %
Shrinkage rate	Shrinkage rate 3.20 mm，Flow	Internal Method	0.20 - 0.50 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Water absorption rate

24 hr

ASTM D570

0.060 %

Shrinkage rate

3.20 mm，Flow

Internal Method

0.20 - 0.50 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot wire ignition	Hot wire ignition	UL 746	PLC 0
High voltage arc tracing rate	High voltage arc tracing rate	UL 746	PLC 4
High arc combustion index	High arc combustion index	UL 746	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index	UL 746	PLC 1
Arc resistance	Arc resistance	ASTM D495	PLC 7
Dissipation factor	Dissipation factor 60 Hz	ASTM D150	1.6E-3
Dissipation factor	Dissipation factor	Dissipation factor 50 Hz	ASTM D150	1.6E-3
Dielectric constant	Dielectric constant 50 kHz	ASTM D150	2.98
Dielectric constant	Dielectric constant	Dielectric constant 60 Hz	ASTM D150	2.98
Dielectric strength	Dielectric strength 3.20 mm, in Oil	ASTM D149	24 KV/mm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness L -Sale	ASTM D785	106

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

L -Sale

ASTM D785

106

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.