PPO NORYL™ PX9406P-7001 SABIC INNOVATIVE JAPAN

159

Unit Price:
US $ 4,242 /MT
Packaging Specification:
25KG/túi
Packaging Material:
Keo dán túi
Supply Quantity:
5MT (1 Container | Container MT / 20Feet)
COA Certificate:
Provide
Delivery Terms:
CIF
Port Of Destination:
Saigon Port

Material Description

Material Properties:Chống cháy
Typical Applications:Phụ kiện truyền thông điệ｜Phụ kiện truyền thông điệ｜Vật liệu xây dựng｜Hồ sơ
Color:--
Grade:Lớp ép phun

Technical Data Sheet Compare

Filling analysis	Test Condition	Test Method	Test Result
Melt viscosity	Melt viscosity 280°C, 1500 sec^-1	ISO 11443	278 Pa·s

Filling analysis

Test Condition

Test Method

Test Result

Melt viscosity

280°C, 1500 sec^-1

ISO 11443

278 Pa·s

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	9.0 kJ/m²

impact performance

Test Condition

Test Method

Test Result

Impact strength of simply supported beam without notch

-30°C

ISO 179/1eU

9.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	UL flame retardant rating 0.40 mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating 0.75 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating 2.5 mm	UL 94	5VA

flammability

Test Condition

Test Method

Test Result

UL flame retardant rating

0.40 mm

UL 94

V-2

UL flame retardant rating

0.75 mm

UL 94

V-0

UL flame retardant rating

2.5 mm

UL 94

5VA

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	tensile strength Yield	Internal Method	63.0 Mpa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	73.0 Mpa
Tensile strain	Tensile strain Break	Internal Method	85 %
Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2/50	4.5 %
Bending modulus	Bending modulus --	ASTM D790	2350 Mpa
Bending modulus	Bending modulus	Bending modulus --2	ISO 178	2600 Mpa
bending strength	bending strength --	ASTM D790	99.0 Mpa
bending strength	bending strength	bending strength --2,3	ISO 178	108 Mpa

injection	Test Condition	Test Result
drying temperature	drying temperature	105 to 110 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	30 to 70 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	245 to 295 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	255 to 300 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	265 to 305 °C
Spray nozzle temperature	Spray nozzle temperature	275 to 305 °C
Processing (melt) temperature	Processing (melt) temperature	275 to 305 °C
Mold temperature	Mold temperature	70 to 100 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	20 to 100 rpm
Exhaust hole depth	Exhaust hole depth	0.038 to 0.051 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm	ASTM D648	136 °C
	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	125 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span5	ISO 75-2/Af	117 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A120	151 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	142 °C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -30 to 30°C	TMA	7.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ISO 11359-2	6.6E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40°C	ISO 11359-2	7.6E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	melt mass-flow rate 250°C/10.0 kg	ASTM D1238	3.9 g/10 min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/10.0 kg	ISO 1133	27.0 cm3/10min
	Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/5.0 kg	ISO 1133	10.0 cm3/10min
	Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/5.0 kg	ISO 1133	23.0 cm3/10min
Shrinkage rate	Shrinkage rate 3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	Water absorption rate 24 hr	ASTM D570	0.070 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity	Surface resistivity	ASTM D257	1.0E+16 ohms
Dielectric constant	Dielectric constant 60 Hz	ASTM D150	2.80
Dielectric constant	Dielectric constant 50 kHz	ASTM D150	2.80

Electrical performance

Test Condition

Test Method

Test Result

Surface resistivity

ASTM D257

1.0E+16 ohms

Dielectric constant

60 Hz

ASTM D150

2.80

Dielectric constant

50 kHz

ASTM D150

2.80

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.