ABS

ABS TAIRILAC® AG15E1 FCFC TAIWAN

Unit Price:
US $ 1,450 /MT
Packaging Specification:
25KG/túi
Packaging Material:
Keo dán túi
Supply Quantity:
57MT (3 Containers | Containers 19MT / 20Feet)
COA Certificate:
Provide
Delivery Terms:
CIF
Port Of Destination:
Saigon Port
Material Comparison:
ABS TAIRILAC® AG15E1 FORMOSA NINGBO

Material Description

Material Properties:Độ bóng cao
Typical Applications:Hàng gia dụng｜Lĩnh vực điện tử｜Lĩnh vực điện
Color:--
Grade:Lớp ép phun

Material Certification

FDA

MSDS

RoHS

SGS

TDS

Processing

MSDS

RoHS

SVHC

PSC

Technical Data Sheet Compare

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C, 6.35 mm	ASTM D256	140 J/m

impact performance

Test Condition

Test Method

Test Result

Impact strength of cantilever beam gap

23°C, 6.35 mm

ASTM D256

140 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	UL flame retardant rating 1.5 mm	UL 94	HB

flammability

Test Condition

Test Method

Test Result

UL flame retardant rating

1.5 mm

UL 94

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	tensile strength 23°C	ASTM D638	48.0 Mpa
Bending modulus	Bending modulus 23°C	ASTM D790	2750 Mpa
bending strength	bending strength 23°C	ASTM D790	86.0 Mpa

mechanical properties

Test Condition

Test Method

Test Result

tensile strength

23°C

ASTM D638

48.0 Mpa

Bending modulus

23°C

ASTM D790

2750 Mpa

bending strength

23°C

ASTM D790

86.0 Mpa

injection	Test Condition	Test Result
drying temperature	drying temperature	70 to 80 °C
drying time	drying time	2.0 to 3.0 hr
Processing (melt) temperature	Processing (melt) temperature	190 to 230 °C
Mold temperature	Mold temperature	40 to 80 °C
Injection pressure	Injection pressure	68.6 to 108 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 12.7 mm	ASTM D648	86.0 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Annealed3	ASTM D648	100 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/A	103 °C

thermal performance

Test Condition

Test Method

Test Result

Hot deformation temperature

1.8 MPa, Unannealed, 12.7 mm

ASTM D648

86.0 °C

Hot deformation temperature

1.8 MPa, Annealed3

ASTM D648

100 °C

Vicat softening temperature

ISO 306/A

103 °C

Physical properties	Test Condition	Test Method	Test Result
density	density --	ASTM D792	1.05 g/cm³
density	density	density 23°C	ISO 1183	1.05 g/cm³
melt mass-flow rate	melt mass-flow rate 200°C/5.0 kg	ASTM D1238	1.8 g/10 min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 220°C/10.0 kg	ASTM D1238	20 g/10 min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	Rockwell hardness R-Scale, 23°C	ASTM D785	110
Rockwell hardness	Rockwell hardness R -Sale, 23°C	ISO 2039-2	110

hardness

Test Condition

Test Method

Test Result

Rockwell hardness

R-Scale, 23°C

ASTM D785

110

Rockwell hardness

R -Sale, 23°C

ISO 2039-2

110

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.