mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield, 50.0 mm Span4	ASTM D790	68.0 Mpa
bending strength	bending strength	bending strength --5,6	ISO 178	64.0 Mpa
Bending modulus	Bending modulus --5	ISO 178	2060 Mpa
Bending modulus	Bending modulus	Bending modulus 50.0 mm Span4	ASTM D790	2170 Mpa
elongation	elongation Break	ISO 527-2/5	19 %
	elongation	elongation Break3	ASTM D638	60 %
		elongation	elongation Yield	ISO 527-2/5	3.3 %
		elongation	elongation	elongation Yield3	ASTM D638	3.6 %
tensile strength	tensile strength Break	ISO 527-2/5	35.0 Mpa
	tensile strength	tensile strength Break3	ASTM D638	33.0 Mpa
		tensile strength	tensile strength Yield	ISO 527-2/5	43.0 Mpa
		tensile strength	tensile strength	tensile strength Yield3	ASTM D638	40.0 Mpa
Tensile modulus	Tensile modulus --	ISO 527-2/1	2040 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --2	ASTM D638	1970 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	85 to 95 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.040 %
Suggested injection volume	Suggested injection volume	40 to 80 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	230 to 250 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	235 to 255 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	245 to 260 °C
Spray nozzle temperature	Spray nozzle temperature	235 to 255 °C
Processing (melt) temperature	Processing (melt) temperature	255 to 270 °C
Mold temperature	Mold temperature	60 to 85 °C
Back pressure	Back pressure	0.300 to 1.00 Mpa
Screw speed	Screw speed	30 to 80 rpm
Exhaust hole depth	Exhaust hole depth	0.038 to 0.076 mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	89.0 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D152510	98.0 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	102 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	105 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	88.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	90.0 °C
Ball Pressure Test	Ball Pressure Test 98°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	8.4E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	9.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40°C	ISO 11359-2	9.5E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.50 %
Shrinkage rate	Shrinkage rate 3.20 mm，Flow	Internal Method	0.50 - 0.80 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260°C/5.0 kg	ISO 1133	10.0 cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/10.0 kg	ISO 1133	6.00 cm3/10min
melt mass-flow rate	melt mass-flow rate 260°C/5.0 kg	ASTM D1238	11 g/10 min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 220°C/10.0 kg	ASTM D1238	6.3 g/10 min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.