ABS/PC CYCOLOY™ C2950-701NSDD SABIC INNOVATIVE US

261

Unit Price:
₫ 74.450 /KG
Packaging Specification:
25KG/túi
Packaging Material:
Túi giấy
Supply Quantity:
25MT
COA Certificate:
Provide
Place of Delivery:
Miền Nam Việt Nam (xung quanh Hồ Chí Minh)

Material Description

Material Properties:Chống cháy｜Dòng chảy cao｜Chống va đập cao｜Chịu nhiệt độ cao｜Chịu nhiệt
Typical Applications:Lĩnh vực ô tô｜Thiết bị gia dụng｜Lĩnh vực điện tử｜Lĩnh vực điện
Color:--
Grade:Lớp ép phun

Technical Data Sheet Compare

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 30℃	ASTM D256	160 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	ASTM D256	534 J/m
Instrumented dart impact energy -30 ℃ (-22 ℉) peak	Instrumented dart impact energy -30 ℃ (-22 ℉) peak	ASTM D3763	54 J
Instrumented dart impact energy 23 ℃ (73 ℉) total energy	Instrumented dart impact energy 23 ℃ (73 ℉) total energy	ASTM D3763	61 J

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	tensile strength Type I, 50，Yield	ASTM D638	62 Mpa
Elongation at Break	Elongation at Break Type I, 50	ASTM D638	40
bending strength	bending strength 2.6 mm/，Yield	ASTM D790	102 Mpa
Bending modulus	Bending modulus 2.6 mm/	ASTM D790	2650 Mpa

thermal properties	Test Condition	Test Method	Test Result
Vicat softening temperature	Vicat softening temperature Rate B/50	ASTM D1525	85 °C
RTI Imp	RTI Imp	UL 746B	85 °C
RTI Elec	RTI Elec	UL 746B	85 °C
RTI Imp	RTI Imp	UL 746B	85 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -30°C to 3，Flow	ASTM E831	72 E-6/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -30°C to 3，Across Flow	ASTM E831	72 E-6/°C
thermal conductivity	thermal conductivity	ASTM C 177	0.2 W/m-°C

combustion performance	Test Condition	Test Method	Test Result
UL fire rating V	UL fire rating V	UL 94	1.5 mm
UL fire rating 5VB	UL fire rating 5VB	UL 94	2.49 mm
Limiting Oxygen Index (LOI)	Limiting Oxygen Index (LOI)	ASTM D 2863	32 %

combustion performance

Test Condition

Test Method

Test Result

UL fire rating V

UL 94

1.5 mm

UL fire rating 5VB

UL 94

2.49 mm

Limiting Oxygen Index (LOI)

ASTM D 2863

32 %

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	melt mass-flow rate	ASTM D1238	10 g/10min
Shrinkage rate	Shrinkage rate flow, 3.2	Internal	0.4-0.8
Shrinkage rate	Shrinkage rate	Shrinkage rate xflow, 3.2	Internal	0.4-0.6
Water absorption rate	Water absorption rate flow, 3.2	ASTM D570	0.4
Water absorption rate	Water absorption rate	Water absorption rate 24 hours	ASTM D570	0.1

Electrical Property	Test Condition	Test Method	Test Result
Volume resistivity	Volume resistivity	ASTM D257	100000000000000000 ohm-cm
Surface resistivity	Surface resistivity	ASTM D257	10000000000000000 Ohm
Dielectric constant	Dielectric constant	ASTM D 150	3
Dielectric constant	Dielectric constant	Dielectric constant	ASTM D 150	3
Dissipation factor	Dissipation factor	ASTM D 150	50 E-4
Dissipation factor	Dissipation factor	Dissipation factor	ASTM D 150	49 E-4
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI)	UL 746A	PLC_0
Dielectric strength	Dielectric strength in oil, 3.2	ASTM D149	19.5 kV/mm
Arc resistance	Arc resistance	ASTM D495	PLC_6
High voltage arc tracing rate	High voltage arc tracing rate	UL 746A	PLC 2
Hot wire ignition (HWI)	Hot wire ignition (HWI)	UL 746A	PLC_1
High current arc ignition (HAI)	High current arc ignition (HAI)	UL 746A	PLC_0

hardness	Test Condition	Test Method	Test Result
Hardness (Rockwell R)	Hardness (Rockwell R)	ASTM D785	123 R

hardness

Test Condition

Test Method

Test Result

Hardness (Rockwell R)

ASTM D785

123 R

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.