impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	ISO 6603-2	26.9 J
Dart impact	Dart impact 23°C,EnergyatPeakLoad	ASTM D3763	32.8 J
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	16 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break	ASTM D638	6.0 %
Tensile strain	Tensile strain Yield	ISO 527-2	3.0 %
elongation	elongation Yield	ASTM D638	3.1 %
tensile strength	tensile strength Break	ISO 527-2	31.0 Mpa
	tensile strength	tensile strength Break	ASTM D638	36.7 Mpa
		tensile strength	tensile strength Yield	ISO 527-2	38.0 Mpa
		tensile strength	tensile strength	tensile strength Yield	ASTM D638	39.1 Mpa
Tensile modulus	Tensile modulus	ISO 527-2/1	2010 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	2070 Mpa
bending strength	bending strength	ISO 178	59.1 Mpa
bending strength	bending strength	bending strength	ASTM D790	65.7 Mpa
Bending modulus	Bending modulus	ISO 178	1980 Mpa
Bending modulus	Bending modulus	Bending modulus	ASTM D790	2100 Mpa
Tensile strain	Tensile strain Break	ISO 527-2	24 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	88.9 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	91.0 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	76.7 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	76.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	9.3E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	9.3E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 24hr,50%RH	ASTM D570	1.1 %
Shrinkage rate	Shrinkage rate MD:24hr	ISO 294-4	0.41 %
	Shrinkage rate	Shrinkage rate TD:24hr	ISO 294-4	0.49 %
		Shrinkage rate	Shrinkage rate TD：24hr	ASTM D955	0.50 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD：24hr	ASTM D955	0.40 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	ASTM D257	1.0E+9to1.0E+11 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Surface resistivity

ASTM D257

1.0E+9to1.0E+11 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.