mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength	ASTM D-638	500 kg/cm
Elongation at Break	Elongation at Break	ASTM D-638	20 %
Bending modulus	Bending modulus	ASTM D-790	820 kg/cm
Rockwell hardness	Rockwell hardness R-Scale	ASTM D-785	107
Bending modulus	Bending modulus	ASTM D-790	24000 kg/cm
impact elasticity	impact elasticity Notched1/4"	ASTM D-256	11 kgcm/cm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature Unannealed18.5kg/cm2,1/2"	ASTM D-648	113 °C
Vicat softening temperature	Vicat softening temperature 1.000g	ASTM D-1525	137 °C
Burning rate	Burning rate 1/8"	UL -94	HB
	Burning rate	Burning rate 1/8"	IEC 707	FH3-34 mm/min
	Burning rate	Burning rate	Burning rate 1/16"	UL -94	HB

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate	ASTM D-955	0.003-0.005 mm/mm
melt mass-flow rate	melt mass-flow rate 220℃/10kg	ASTM D-1238	4 g/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

ASTM D-955

0.003-0.005 mm/mm

melt mass-flow rate

220℃/10kg

ASTM D-1238

4 g/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot wire ignition	Hot wire ignition	UL -746A	PLC 5
High arc combustion index	High arc combustion index	UL -746A	PLC 0
High voltage arc tracing rate	High voltage arc tracing rate	UL -746A	PLC 2
Arc resistance	Arc resistance	ASTM D-495	PLC_6

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.