Material Properties:Độ nhớt cao｜Chống mài mòn｜Trong suốt｜Dòng chảy cao｜Thời tiết kháng｜phổ quát
Typical Applications:Lĩnh vực điện｜Lĩnh vực điện tử｜Thiết bị gia dụng｜Thiết bị gia dụng
Color:--
Grade:Lớp ép phun

Technical Data Sheet Compare

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	6.0 kJ/m²

impact performance

Test Condition

Test Method

Test Result

Charpy Notched Impact Strength

23°C

ISO 179/1eA

6.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	UL flame retardant rating	UL 94	HB

flammability

Test Condition

Test Method

Test Result

UL flame retardant rating

UL 94

mechanical properties	Test Condition	Test Method	Test Result
Wear factor	Wear factor 0.060MPa,0.15m/sec8	JISK7218	6500 10^-8mm³/N·m
	Wear factor	Wear factor 0.060MPa,0.15m/sec7	JISK7218	3500 10^-8mm³/N·m
		Wear factor	Wear factor 0.49MPa,0.30m/sec6	JISK7218	65 10^-8mm³/N·m
			Wear factor	Wear factor 0.98MPa,0.30m/sec6	JISK7218	30 10^-8mm³/N·m
				Wear factor	Wear factor 0.49MPa,0.30m/sec5	JISK7218	<1.0 10^-8mm³/N·m
				Wear factor	Wear factor	Wear factor 0.98MPa,0.30m/sec5	JISK7218	<1.0 10^-8mm³/N·m
Friction coefficient	Friction coefficient Steel - Dynamic4	JISK7218	0.40
	Friction coefficient	Friction coefficient Steel - Dynamic3	JISK7218	0.46
	Friction coefficient	Friction coefficient	Friction coefficient Dynamic2	JISK7218	0.37
bending strength	bending strength	ISO 178	87.0 Mpa
Bending modulus	Bending modulus	ISO 178	2500 Mpa
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	35 %
tensile strength	tensile strength	ISO 527-2	62.0 Mpa
Tensile modulus	Tensile modulus	ISO 527-2	2700 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	Internal Method	1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	Internal Method	1.2E-04 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	95.0 °C

thermal performance

Test Condition

Test Method

Test Result

Linear coefficient of thermal expansion

MD：23to55°C

Internal Method

1.2E-04 cm/cm/°C

Linear coefficient of thermal expansion

TD：23to55°C

Internal Method

1.2E-04 cm/cm/°C

Hot deformation temperature

1.8MPa,Unannealed

ISO 75-2/A

95.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.50 %
Shrinkage rate	Shrinkage rate MD:2.00mm	ISO 294-4	2.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD:2.00mm	ISO 294-4	2.0 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 190°C/2.16kg	ISO 1133	8.00 cm3/10min
melt mass-flow rate	melt mass-flow rate	ISO 1133	9.0 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate	ASTM D1238	9.0 g/10min
density	density	ISO 1183	1.41 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity	Surface resistivity	IEC 60093	1E+16 ohms
Volume resistivity	Volume resistivity	IEC 60093	1E+14 ohms·cm
Dielectric strength	Dielectric strength 3.00mm	IEC 60243-1	19 KV/mm

Electrical performance

Test Condition

Test Method

Test Result

Surface resistivity

IEC 60093

1E+16 ohms

Volume resistivity

IEC 60093

1E+14 ohms·cm

Dielectric strength

3.00mm

IEC 60243-1

19 KV/mm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	Rockwell hardness M-Scale	ISO 2039-2	80

hardness

Test Condition

Test Method

Test Result

Rockwell hardness

M-Scale

ISO 2039-2

Supplementary Information	Test Condition	Test Method	Test Result
ColourNumber	ColourNumber		CF2001/CD3068

Supplementary Information

Test Condition

Test Method

Test Result

ColourNumber

CF2001/CD3068

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.