mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D-256	256 J/m
tensile strength	tensile strength Yield点，3.2mm	ASTM D-638	58 Mpa
tensile strength	tensile strength	tensile strength Break点，3.2mm	ASTM D-638	25 Mpa
bending strength	bending strength 6.4mm	ASTM D-790	83 Mpa
Rockwell hardness	Rockwell hardness	ASTM D-785	115
Bending modulus	Bending modulus 6.4mm	ASTM D-790	2308 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Hot deformation temperature 0.45MPa	ASTM D-648	102-110 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa	ASTM D-648	92-100 °C
Long term use temperature	Long term use temperature 电气	UL 746B	95 °C
	Long term use temperature	Long term use temperature 含冲击	UL 746B	85 °C
	Long term use temperature	Long term use temperature	Long term use temperature 无冲击	UL 746B	95 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	Shrinkage rate 3.2mm	ASTM D-955	5-7

Physical properties

Test Condition

Test Method

Test Result

Shrinkage rate

3.2mm

ASTM D-955

5-7

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity	Surface resistivity	ASTM D-257	1.0×10 Ω.cm
Volume resistivity	Volume resistivity	ASTM D-257	3.0×10 Ω.cm
Dielectric constant	Dielectric constant 1MHz	ASTM D-150	2.57

Electrical performance

Test Condition

Test Method

Test Result

Surface resistivity

ASTM D-257

1.0×10 Ω.cm

Volume resistivity

ASTM D-257

3.0×10 Ω.cm

Dielectric constant

1MHz

ASTM D-150

2.57

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PPO NORYL™ SE100X-701 SABIC INNOVATIVE SHANGHAI

Material Description

Material Certification

Technical Data Sheet Compare

Other Quotes