mechanical properties	Test Condition	Test Method	Test Result
tensile strength	tensile strength Yield	ASTM D638	31.4 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	39.2 Mpa
elongation	elongation Break	ASTM D638	1000 %
Bending modulus	Bending modulus	ASTM D747	981 Mpa
Bending modulus	Bending modulus	Bending modulus	ASTM D790	1370 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	Vicat softening temperature	ASTM D15253	125 °C
Melting temperature	Melting temperature	ASTM D3418	133 °C

thermal performance

Test Condition

Test Method

Test Result

Vicat softening temperature

ASTM D15253

125 °C

Melting temperature

ASTM D3418

133 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	melt mass-flow rate 190°C/2.16kg	ASTM D1238	0.40 g/10min
Environmental stress cracking resistance	Environmental stress cracking resistance 25%Igepal,F50	ASTM D1693B	400 hr

Physical properties

Test Condition

Test Method

Test Result

melt mass-flow rate

190°C/2.16kg

ASTM D1238

0.40 g/10min

Environmental stress cracking resistance

25%Igepal,F50

ASTM D1693B

400 hr

hardness	Test Condition	Test Method	Test Result
Shore hardness	Shore hardness ShoreD	ASTM D2240	65

hardness

Test Condition

Test Method

Test Result

Shore hardness

ShoreD

ASTM D2240

IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.