impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	15 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	5.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	75.0 Mpa
Bending modulus	Bending modulus	ISO 178	2200 Mpa
Tensile strain	Tensile strain Break	ISO 527-2/50	30 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/50	5.0 %
tensile strength	tensile strength Break	ISO 527-2/50	50.0 Mpa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	55.0 Mpa
Tensile modulus	Tensile modulus	ISO 527-2/1	2300 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	280 to 300 °C
Spray nozzle temperature	Spray nozzle temperature	260 to 280 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	260 to 280 °C
Temperature at the rear of the barrel	Temperature at the rear of the barrel	240 to 260 °C
Hopper temperature	Hopper temperature	60 to 80 °C
drying time	drying time	2.0 to 3.0 hr
drying temperature	drying temperature	100 to 120 °C
Processing (melt) temperature	Processing (melt) temperature	280 to 300 °C
Mold temperature	Mold temperature	80 to 120 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : 23 to 80°C	ISO 11359-2	7.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : 23 to 80°C	ISO 11359-2	7.0E-5 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	140 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	135 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	115 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.060 %
Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.23 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/5.0 kg	ISO 1133	8.00 cm3/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Water absorption rate

Equilibrium, 23°C, 50% RH

ISO 62

0.060 %

Water absorption rate

Saturation, 23°C

ISO 62

0.23 %

Melt Volume Flow Rate (MVR)

280°C/5.0 kg

ISO 1133

8.00 cm3/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.