PPO NORYL™  731S-701 SABIC INNOVATIVE SHANGHAI

187
  • Unit Price:
    US $ 4,242 /MT
  • Packaging Specification:
    25KG/túi
  • Packaging Material:
    Keo dán túi
  • Supply Quantity:
    5MT (1 Container | Container MT / 20Feet)
  • COA Certificate:
    Provide
  • Delivery Terms:
    CIF
  • Port Of Destination:
    Saigon Port
Material Description
Technical Data Sheet

Material Description

  • Material Properties:Dòng chảy caoChống tĩnh điệnChịu nhiệt độ caophổ quát
  • Typical Applications:Hộp đựng thực phẩm
  • Color:--
  • Grade:Lớp ép phun

Technical Data Sheet Compare

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength

Charpy Notched Impact Strength

-30°C

ISO 179/1eA5.0 kJ/m²
Charpy Notched Impact Strength

Charpy Notched Impact Strength

23°C

ISO 179/1eA15 kJ/m²
Impact strength of cantilever beam gap

Impact strength of cantilever beam gap

-30°C

ISO 180/1A5.0 kJ/m²
Impact strength of cantilever beam gap

Impact strength of cantilever beam gap

23°C

ISO 180/1A15 kJ/m²
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus

Tensile modulus

ISO 527-2/12300 Mpa
tensile strength

tensile strength

Yield

ISO 527-2/5055.0 Mpa
tensile strength

tensile strength

Break

ISO 527-2/5050.0 Mpa
Tensile strain

Tensile strain

Yield

ISO 527-2/505.0 %
Tensile strain

Tensile strain

Break

ISO 527-2/5030 %
Bending modulus

Bending modulus

ISO 1782200 Mpa
bending strength

bending strength

ISO 17875.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature

drying temperature

100 to 120 °C
drying time

drying time

2.0 to 3.0 hr
Hopper temperature

Hopper temperature

60 to 80 °C
Temperature at the rear of the barrel

Temperature at the rear of the barrel

240 to 260 °C
Temperature in the middle of the barrel

Temperature in the middle of the barrel

260 to 280 °C
Temperature at the front of the material cylinder

Temperature at the front of the material cylinder

280 to 300 °C
Spray nozzle temperature

Spray nozzle temperature

260 to 280 °C
Processing (melt) temperature

Processing (melt) temperature

280 to 300 °C
Mold temperature

Mold temperature

80 to 120 °C
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature

Hot deformation temperature

1.8 MPa, Unannealed, 4.00 mm, 100 mm Span

ISO 75-2/Ae115 °C
Vicat softening temperature

Vicat softening temperature

--

ISO 306/B50135 °C
Vicat softening temperature

Vicat softening temperature

--

ISO 306/B120140 °C
Linear coefficient of thermal expansion

Linear coefficient of thermal expansion

Flow : 23 to 80°C

ISO 11359-27.0E-5 cm/cm/°C
Linear coefficient of thermal expansion

Linear coefficient of thermal expansion

Across Flow : 23 to 80°C

ISO 11359-27.0E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Melt Volume Flow Rate (MVR)

Melt Volume Flow Rate (MVR)

280°C/5.0 kg

ISO 11338.00 cm3/10min
Water absorption rate

Water absorption rate

Saturation, 23°C

ISO 620.23 %
Water absorption rate

Water absorption rate

Equilibrium, 23°C, 50% RH

ISO 620.060 %
IMPORTANT NOTES: vnplas.com collected the data in the data sheet from the material manufacturers. vnplas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.