空气中拉伸强度的变化率 | 150°C,168hr | ASTMD573 | -29 | % |
空气中拉伸强度的变化率 | 150°C,168hr | ISO188 | -29 | % |
空气中极限伸长率的变化率 | 150°C,168hr | ASTMD573 | -1.0 | % |
ChangeinDurometerHardnessinAir | ShoreA,150°C,168hr | ASTMD573 | -1.0 | |
ChangeinShoreHardnessinAir | ShoreA,150°C,168hr | ISO188 | -1.0 | |
拉伸强度的变化率 | 23°C,168hr,inAceticAcid | ASTMD471 | -6.0 | % |
拉伸强度的变化率 | 23°C,168hr,inCyclohexane | ASTMD471 | 4040 | % |
拉伸强度的变化率 | 23°C,168hr,inDetergent(Tide),2.5% | ASTMD471 | -6.0 | % |
拉伸强度的变化率 | 23°C,168hr,inEthanol,95% | ASTMD471 | -8.0 | % |
极限伸长率的变化率 | 23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | 0.0 | % |
极限伸长率的变化率 | 23°C,168hr,inIsopropylAlcohol | ASTMD471 | 53 | % |
极限伸长率的变化率 | 23°C,168hr,inMethylethylketone | ASTMD471 | 80 | % |
极限伸长率的变化率 | 23°C,168hr,inSodiumChloride,15% | ASTMD471 | -7.0 | % |
极限伸长率的变化率 | 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | -3.0 | % |
极限伸长率的变化率 | 23°C,168hr,inSulfuricAcid,98% | ASTMD471 | -10 | % |
极限伸长率的变化率 | 23°C,168hr,inTrichloroethylene | ASTMD471 | 77 | % |
极限伸长率的变化率 | 100°C,168hr,inDeionizedWater | ASTMD471 | -17 | % |
极限伸长率的变化率 | 100°C,168hr,inIRM903Oil | ASTMD471 | -63 | % |
极限伸长率的变化率 | 125°C,70hr,inIRM903Oil | ASTMD471 | -65 | % |
拉伸强度的变化率 | 125°C,168hr,inIRM903Oil | ASTMD471 | -67 | % |
拉伸强度的变化率 | 23°C,168hr,inAceticAcid | ISO1817 | -6.0 | % |
拉伸强度的变化率 | 23°C,168hr,inCyclohexane | ISO1817 | 4040 | % |
拉伸强度的变化率 | 23°C,168hr,inDetergent(Tide),2.5% | ISO1817 | -6.0 | % |
拉伸强度的变化率 | 23°C,168hr,inEthanol,95% | ISO1817 | -8.0 | % |
拉伸强度的变化率 | 23°C,168hr,inHydrochloricAcid,10% | ISO1817 | -6.0 | % |
拉伸强度的变化率 | 23°C,168hr,inIsopropylAlcohol | ISO1817 | 27 | % |
拉伸强度的变化率 | 23°C,168hr,inMethylethylketone | ISO1817 | 43 | % |
拉伸强度的变化率 | 23°C,168hr,inSodiumChloride,15% | ISO1817 | -14 | % |
拉伸强度的变化率 | 23°C,168hr,inSodiumHydroxide,50% | ISO1817 | -5.0 | % |
质量变化率 | 23.0°C,168hr,inTrichloroethylene | ISO1817 | -20 | % |
质量变化率 | 23.0°C,168hr,inCyclohexane | ISO1817 | -11 | % |
质量变化率 | 23.0°C,168hr,inSodiumHydroxide,50% | ISO1817 | -0.30 | % |
质量变化率 | 23.0°C,168hr,inSodiumChloride,15% | ISO1817 | 0.10 | % |
质量变化率 | 23.0°C,168hr,inHydrochloricAcid,10% | ISO1817 | 0.20 | % |
质量变化率 | 23.0°C,168hr,inEthanol,95% | ISO1817 | 0.20 | % |
质量变化率 | 23.0°C,168hr,inDetergent(Tide),2.5% | ISO1817 | 0.90 | % |
质量变化率 | 100°C,168hr,inDeionizedWater | ISO1817 | 6.2 | % |
质量变化率 | 23.0°C,168hr,inAceticAcid | ISO1817 | 6.9 | % |
质量变化率 | 23.0°C,168hr,inSulfuricAcid,98% | ISO1817 | 7.2 | % |
ChangeinShoreHardness | ShoreA,23°C,168hr,inAceticAcid | ISO1817 | -1.0 | |
ChangeinShoreHardness | ShoreA,23°C,168hr,inCyclohexane | ISO1817 | -11 | |
ChangeinShoreHardness | ShoreA,23°C,168hr,inDetergent(Tide),2.5% | ISO1817 | 2.0 | |
ChangeinShoreHardness | ShoreA,23°C,168hr,inEthanol,95% | ISO1817 | 1.0 | |
ChangeinShoreHardness | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ISO1817 | -1.0 | |
ChangeinShoreHardness | ShoreA,23°C,168hr,inIsopropylAlcohol | ISO1817 | 5.0 | |
ChangeinShoreHardness | ShoreA,23°C,168hr,inMethylethylketone | ISO1817 | 15 | |
ChangeinShoreHardness | ShoreA,23°C,168hr,inSodiumChloride,15% | ISO1817 | 2.0 | |
ChangeinShoreHardness | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO1817 | 4.0 | |
ChangeinShoreHardness | ShoreA,23°C,168hr,inSulfuricAcid,98% | ISO1817 | -2.0 | |
质量变化率 | 23°C,168hr,inMethylethylketone | ASTMD471 | -41 | % |
质量变化率 | 23°C,168hr,inSodiumChloride,15% | ASTMD471 | 0.10 | % |
质量变化率 | 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | -0.30 | % |
质量变化率 | 23°C,168hr,inSulfuricAcid,98% | ASTMD471 | 7.2 | % |
质量变化率 | 23°C,168hr,inTrichloroethylene | ASTMD471 | -20 | % |
质量变化率 | 100°C,168hr,inDeionizedWater | ASTMD471 | 6.2 | % |
质量变化率 | 100°C,168hr,inIRM903Oil | ASTMD471 | 93 | % |
质量变化率 | 125°C,168hr,inIRM903Oil | ASTMD471 | 100 | % |
质量变化率 | 23.0°C,168hr,inMethylethylketone | ISO1817 | -41 | % |
质量变化率 | 23.0°C,168hr,inIsopropylAlcohol | ISO1817 | -25 | % |
拉伸强度的变化率 | 23°C,168hr,inSulfuricAcid,98% | ISO1817 | -47 | % |
拉伸强度的变化率 | 23°C,168hr,inTrichloroethylene | ISO1817 | 56 | % |
拉伸强度的变化率 | 100°C,168hr,inDeionizedWater | ISO1817 | -18 | % |
拉伸强度的变化率 | 100°C,168hr,inIRM903Oil | ISO1817 | -57 | % |
拉伸强度的变化率 | 125°C,70hr,inIRM903Oil | ISO1817 | -61 | % |
拉伸强度的变化率 | 125°C,168hr,inIRM903Oil | ISO1817 | -67 | % |
极限伸长率的变化率 | 23°C,168hr,inAceticAcid | ASTMD471 | -3.0 | % |
极限伸长率的变化率 | 23°C,168hr,inCyclohexane | ASTMD471 | 63 | % |
极限伸长率的变化率 | 23°C,168hr,inDetergent(Tide),2.5% | ASTMD471 | 0.0 | % |
极限伸长率的变化率 | 23°C,168hr,inEthanol,95% | ASTMD471 | 3.0 | % |
拉伸强度的变化率 | 23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | -6.0 | % |
拉伸强度的变化率 | 23°C,168hr,inIsopropylAlcohol | ASTMD471 | 27 | % |
拉伸强度的变化率 | 23°C,168hr,inMethylethylketone | ASTMD471 | 43 | % |
拉伸强度的变化率 | 23°C,168hr,inSodiumChloride,15% | ASTMD471 | -14 | % |
拉伸强度的变化率 | 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | -5.0 | % |
拉伸强度的变化率 | 23°C,168hr,inSulfuricAcid,98% | ASTMD471 | -47 | % |
拉伸强度的变化率 | 23°C,168hr,inTrichloroethylene | ASTMD471 | 56 | % |
拉伸强度的变化率 | 100°C,168hr,inDeionizedWater | ASTMD471 | -18 | % |
拉伸强度的变化率 | 100°C,168hr,inIRM903Oil | ASTMD471 | -57 | % |
拉伸强度的变化率 | 125°C,70hr,inIRM903Oil | ASTMD471 | -61 | % |
极限伸长率的变化率 | 125°C,168hr,inIRM903Oil | ASTMD471 | -70 | % |
断裂时拉伸应力变化 | 23°C,168hr,inAceticAcid | ISO1817 | -3.0 | % |
断裂时拉伸应力变化 | 23°C,168hr,inCyclohexane | ISO1817 | 63 | % |
断裂时拉伸应力变化 | 23°C,168hr,inDetergent(Tide),2.5% | ISO1817 | 0.0 | % |
断裂时拉伸应力变化 | 23°C,168hr,inEthanol,95% | ISO1817 | 3.0 | % |
断裂时拉伸应力变化 | 23°C,168hr,inHydrochloricAcid,10% | ISO1817 | 0.0 | % |
断裂时拉伸应力变化 | 23°C,168hr,inIsopropylAlcohol | ISO1817 | 53 | % |
断裂时拉伸应力变化 | 23°C,168hr,inMethylethylketone | ISO1817 | 80 | % |
断裂时拉伸应力变化 | 23°C,168hr,inSodiumChloride,15% | ISO1817 | -7.0 | % |
断裂时拉伸应力变化 | 23°C,168hr,inSodiumHydroxide,50% | ISO1817 | -3.0 | % |
ChangeinShoreHardness | ShoreA,23°C,168hr,inTrichloroethylene | ISO1817 | 1.0 | |
ChangeinShoreHardness | ShoreA,100°C,168hr,inDeionizedWater | ISO1817 | 0.0 | |
ChangeinShoreHardness | ShoreA,100°C,168hr,inIRM903Oil | ISO1817 | -26 | |
ChangeinShoreHardness | ShoreA,125°C,168hr,inIRM903Oil | ISO1817 | -30 | |
质量变化率 | 23°C,168hr,inAceticAcid | ASTMD471 | 6.9 | % |
质量变化率 | 23°C,168hr,inCyclohexane | ASTMD471 | -11 | % |
质量变化率 | 23°C,168hr,inDetergent(Tide),2.5% | ASTMD471 | 0.90 | % |
质量变化率 | 23°C,168hr,inEthanol,95% | ASTMD471 | 0.20 | % |
质量变化率 | 23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | 0.20 | % |
质量变化率 | 23°C,168hr,inIsopropylAlcohol | ASTMD471 | -25 | % |
质量变化率 | 100°C,168hr,inIRM903Oil | ISO1817 | 93 | % |
质量变化率 | 125°C,168hr,inIRM903Oil | ISO1817 | 100 | % |
体积变化 | 125°C,70hr,在IRM903油中 | ASTMD471 | 110 | % |
体积变化 | 125°C,70hr,在IRM903油中 | ISO1817 | 110 | % |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ASTMD471 | -1.0 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inIsopropylAlcohol | ASTMD471 | 5.0 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inMethylethylketone | ASTMD471 | 15 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inSodiumChloride,15% | ASTMD471 | 2.0 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | 4.0 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inSulfuricAcid,98% | ASTMD471 | -2.0 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inTrichloroethylene | ASTMD471 | 1.0 | |
硬度计硬度的变化率2 | ShoreA,100°C,168hr,inDeionizedWater | ASTMD471 | 0.0 | |
硬度计硬度的变化率2 | ShoreA,100°C,168hr,inIRM903Oil | ASTMD471 | -26 | |
硬度计硬度的变化率2 | ShoreA,125°C,168hr,inIRM903Oil | ASTMD471 | -30 | |
断裂时拉伸应力变化 | 23°C,168hr,inSulfuricAcid,98% | ISO1817 | -10 | % |
断裂时拉伸应力变化 | 23°C,168hr,inTrichloroethylene | ISO1817 | 77 | % |
断裂时拉伸应力变化 | 23°C,168hr,inTrichloroethylene | ISO1817 | 77 | % |
断裂时拉伸应力变化 | 100°C,168hr,inDeionizedWater | ISO1817 | -17 | % |
断裂时拉伸应力变化 | 100°C,168hr,inIRM903Oil | ISO1817 | -63 | % |
断裂时拉伸应力变化 | 125°C,70hr,inIRM903Oil | ISO1817 | -65 | % |
断裂时拉伸应力变化 | 125°C,168hr,inIRM903Oil | ISO1817 | -70 | % |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inAceticAcid | ASTMD471 | -1.0 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inAceticAcid | ASTMD471 | -1.0 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inCyclohexane | ASTMD471 | -11 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inDetergent(Tide),2.5% | ASTMD471 | 2.0 | |
硬度计硬度的变化率2 | ShoreA,23°C,168hr,inEthanol,95% | ASTMD471 | 1.0 | |