Melt Mass-Flow Rate

300°C/1.2 kg

ASTM D1238

g/10 min

1

Melt Volume flow Rate

300°C/1.2 kg

ISO 1133

cm3/10min

1

Modeling Shrinkage

流动 : 3.20 mm

内部方法

%

0

Modeling Shrinkage

横向流动 : 3.20 mm

内部方法

%

0

Moisture Absorption

饱和, 23°C

ISO 62

%

0

Moisture Absorption

平衡, 23°C, 50% RH

ISO 62

%

0

Tensile Strength

屈服 3

ASTM D638

Mpa

5

Tensile Strength

屈服

ISO 527-2/50

Mpa

5

Tensile Strength

断裂 3

ASTM D638

Mpa

5

Tensile Strength

断裂

ISO 527-2/50

Mpa

5

Tensile Modulus

-- 2

ASTM D638

Mpa

2

Tensile Modulus

--

ISO 527-2/1

Mpa

2

Tensile Elongation

屈服 3

ASTM D638

%

5

Tensile Elongation

屈服

ISO 527-2/50

%

5

Tensile Elongation

断裂 3

ASTM D638

%

1

Tensile Elongation

断裂

ISO 527-2/50

%

1

Flexural Modulus

50.0 mm 跨距 4

ASTM D790

Mpa

2

Flexural Modulus

-- 5

ISO 178

Mpa

2

Flexural Stress

-- 5, 6

ISO 178

Mpa

8

Flexural Stress

屈服, 50.0 mm 跨距 4

ASTM D790

Mpa

9

RTI

UL 746

°C

1

RTI Elec

UL 746

°C

1

RTI Imp

UL 746

°C

1

Vicat Softening Temperature

--

ASTM D152511, ISO 306/B5011

°C

1

Vicat Softening Temperature

--

ISO 306/B120

°C

1

Coefficient of Linear Thermal Expansion

流动 : -40 到 40°C

ASTM E831

cm/cm/°C

7

Coefficient of Linear Thermal Expansion

流动 : 23 到 80°C

ISO 11359-2

cm/cm/°C

7

Coefficient of Linear Thermal Expansion

横向 : -40 到 40°C

ASTM E831

cm/cm/°C

7

Coefficient of Linear Thermal Expansion

横向 : 23 到 80°C

ISO 11359-2

cm/cm/°C

7

Deflection Temperature Under Load 

0.45 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Deflection Temperature Under Load 

0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10

ISO 75-2/Be

°C

1

Deflection Temperature Under Load 

1.8 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Deflection Temperature Under Load 

1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10

ISO 75-2/Ae

°C

1

Dielectric Strength

3.20 mm, 在油中

IEC 60243-1

KV/mm

1

Comparative Tracking Index

IEC 60112

V

1

Charpy Notched Impact Strength

-30°C

ISO 179/1eA

kJ/m²

2

Charpy Notched Impact Strength

23°C

ISO 179/1eA

kJ/m²

6

Instrumented Dart Impact

23°C, Total Energy

ASTM D3763

J

6

Ball Indentation Hardness

H 358/30

ISO 2039-1

Mpa

9

Oxygen Index

ISO 4589-2

%

4

Glow Wire Ignition Temperature

1.0 mm

IEC 60695-2-13

°C

8

Glow Wire Flammability Index

1.0 mm

IEC 60695-2-12

°C

9

Back Pressure

Mpa

0

Drying Time

hr

3

Drying Temperature

°C

1

Processing (Melt) Temp

°C

2

Suggested Max Moisture

%

0

Suggested Shot Size

%

4

Rear Temperature

°C

2

Front Temperature

°C

2

Middle Temperature

°C

2

Screw Speed

rpm

4

Mold Temperature

°C

7

Vent Depth

mm

0

Nozzle Temperature

°C

2