Modeling Shrinkage

流动 : 1.50 到 3.20 mm

内部方法

%

0

Modeling Shrinkage

流动 : 3.20 到 4.60 mm

内部方法

%

0

Modeling Shrinkage

横向流动 : 1.50 到 3.20 mm

内部方法

%

0

Modeling Shrinkage

横向流动 : 3.20 到 4.60 mm

内部方法

%

0

Specific Volume

ASTM D792

cm³/g

0

Moisture Absorption

24 hr

ASTM D570

%

0

Tensile Strength

断裂

ASTM D638

Mpa

1

Flexural Modulus

50.0 mm 跨距

ASTM D790

Mpa

6

Flexural Strength

断裂, 50.0 mm 跨距

ASTM D790

Mpa

1

RTI

UL 746

°C

1

RTI Elec

UL 746

°C

1

RTI Imp

UL 746

°C

1

Coefficient of Linear Thermal Expansion (Flow)

-40 到 40°C

ASTM E831

cm/cm/°C

2

Coefficient of Linear Thermal Expansion (Flow)

60 到 138°C

ASTM E831

cm/cm/°C

1

Deflection Temperature Under Load 

0.45 MPa, 未退火, 6.40 mm

ASTM D648

°C

2

Deflection Temperature Under Load 

1.8 MPa, 未退火, 6.40 mm

ASTM D648

°C

1

Dielectric Strength

1.60 mm, in Oil

ASTM D149

KV/mm

2

Dielectric Strength

3.20 mm, in Air

ASTM D149

KV/mm

2

Volume Resistivity

ASTM D257

ohms·cm

5

Unnotched Izod Impact Strength

23°C

ASTM D4812

J/m

6

Instrumented Dart Impact

23°C, Energy at Peak

ASTM D3763

J

6

Instrumented Dart Impact

23°C, Total Energy

ASTM D3763

J

8

Back Pressure

Mpa

0

Drying Time

hr

3

Drying Temperature

°C

1

Processing (Melt) Temp

°C

2

Suggested Max Moisture

%

0

Suggested Shot Size

%

4

Rear Temperature

°C

2

Front Temperature

°C

2

Middle Temperature

°C

2

Screw Speed

rpm

5

Mold Temperature

°C

6

Vent Depth

mm

0

Nozzle Temperature

°C

2